The formation of three phases containing Fe and Mn in 5182 aluminum alloy
Ni Tian,Yaozhong Zhang,Zhiyong He,Hao Liu,Zhisen Zhang,Jiacheng Liu,Gang Zhao,Gaowu Qin
DOI: https://doi.org/10.1016/j.matchar.2023.113497
IF: 4.537
2023-11-28
Materials Characterization
Abstract:The categories, crystal types, morphology, dimension, distribution and selectivity of precipitation positions of alloy phases containing Fe and Mn in the DC casting ingot of 5182 aluminum alloy under industrial production conditions after being treated with different homogenization processes were studied through TEM and EPMA with FIB sample preparation. The formation process of three phases containing Fe and Mn was clarified as well. The results showed that there was only one category of alloy phase containing Fe and Mn in the as-cast 5182 aluminum alloy, which was one category of skeletal nonequilibrium constituent Al 19 (Fe,Mn) 4 ′ with orthorhombic structure formed by the eutectic reaction L → α(Al)' + Al 19 (Fe,Mn) 4 ′. After the ingot was homogenized at a high temperature above 460 °C, there were three categories of alloy phases containing Fe and Mn, which were skeletal equilibrium phase Al 19 (Fe,Mn) 4 with orthorhombic structure, short rod-like intermetallic phase Al 3 (Fe,Mn) with monoclinic structure and acicular alloy phase Al 6 (Fe,Mn) with orthorhombic structure, respectively. The metastable constituent Al 19 (Fe,Mn) 4 ′ transformed into the equilibrium phase Al 19 (Fe,Mn) 4 with orthorhombic structure and the alloy phase Al 3 (Fe,Mn) with monoclinic structure by desolation transformation Al 19 (Fe,Mn) 4 ' → Al 19 (Fe,Mn) 4 + Al 3 (Fe,Mn). In addition, acicular alloy phase particles Al 6 (Fe,Mn) with orthorhombic structure were precipitated from the alloy matrix with supersaturated solute Fe and Mn atoms through the desolation reaction α(Al)' → α(Al) + Al 6 (Fe,Mn). With increasing homogenization temperature, the skeletal constituent Al 19 (Fe,Mn) 4 particles with orthorhombic structure were almost the same, and the short rod-like alloy phase Al 3 (Fe,Mn) particles, with monoclinic structure changed unobviously in morphology and size, but its number increased significantly. At the same time, the number and the size of acicular Al 6 (Fe,Mn) alloy phase particles with orthorhombic structure precipitated from the alloy matrix increased.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing