Abstract:Graphitic carbons with ordered mesostructure and high surface areas (of great interest in applications such as energy storage) have been synthesized by a direct triblock‐copolymer‐templating method. Pluronic F127 is used as a structure‐directing agent, with a low‐molecular‐weight phenolic resol as a carbon source, ferric oxide as a catalyst, and silica as an additive. Inorganic oxides can be completely eliminated from the carbon. Small‐angle XRD and N2 sorption analysis show that the resultant carbon materials possess an ordered 2D hexagonal mesostructure, uniform bimodal mesopores (about 1.5 and 6 nm), high surface area (∼1300 m2/g), and large pore volumes (∼1.50 cm3/g) after low‐temperature pyrolysis (900 °C). All surface areas come from mesopores. Wide‐angle XRD patterns demonstrate that the presence of the ferric oxide catalyst and the silica additive lead to a marked enhancement of graphitic ordering in the framework. Raman spectra provide evidence of the increased content of graphitic sp2 carbon structures. Transmission electron microscopy images confirm that numerous domains in the ordered mesostructures are composed of characteristic graphitic carbon nanostructures. The evolution of the graphitic structure is dependent on the temperature and the concentrations of the silica additive, and ferric oxide catalyst. Electrochemical measurements performed on this graphitic mesoporous carbon when used as an electrode material for an electrochemical double layer capacitor shows rectangular‐shaped cyclic voltammetry curves over a wide range of scan rates, even up to 200 mV/s, with a large capacitance of 155 F/g in KOH electrolyte. This method can be widely applied to the synthesis of graphitized carbon nanostructures.

Synthesis of Iron-Dispersed Carbons by Pressure Pyrolysis of Divinylbenzene-Vinylferrocene Copolymer

Synthesis and Properties of Carbons Dispersed with Α-Iron Particles from Divinylbenzene-Vinylferrocene

Synthesis Of Cobaltferrite-Dispersed Carbons By Pressure Pyrolysis Of Organometallic Copolymers

Synthesis and Properties of Magnetite-Dispersed Carbon by Pressure Pyrolysis of Divinylbenzene Vinylferrocene with Water

Synthesis of Carbon/Ferrite Composite by In-Situ Pressure Pyrolysis of Organometallic Polymers

Cementite Dispersed in Carbons from Ferrocene, Vinylferrocene, Divinylbenzene Systems

Synthesis of Functional Carbons by Pressure Pyrolysis of Organometallic Compounds.

Synthesis and Properties of Nickel-Dispersed Carbons by Pressure Pyrolysis of Nickelocene-Divinylbenzene

Synthesis and Properties of Cobalt-Dispersed Carbons by Pressure Pyrolysis of Organocobalt Polymers

Formation of Non-Graphitizable Isotropic Spherulitic Carbon from Poly-Divinylbenzene by Pressure Pyrolysis

Synthesis and Magnetic Properties of Fe3O4/helical Carbon Nanofiber Nanocomposites from the Catalytic Pyrolysis of Ferrocene

Synthesis of Boron-Dispersed Carbon by Pressure Pyrolysis of Organoborane Copolymer

Tuning the Properties of Iron-Doped Porous Graphitic Carbon Synthesized by Hydrothermal Carbonization of Cellulose and Subsequent Pyrolysis

Humidity-Controlled Preparation of Flexible Porous Carbon Fibers from Block Copolymers

Phase Diagram and Transformations of Iron Pentacarbonyl to nm Layered Hematite and Carbon-Oxygen Polymer under Pressure

Synthesis of Carbon/Carbon Core/Shell Nanofibers by Co-Pyrolysis of Tetrahydrofuran and Ferrocene

Synthesis and Properties of Platinum-Dispersed Carbon by Pressure Pyrolysis of Organoplatinum Copolymer

Direct Synthesis of Porous Carbon Materials Prepared from Diethyldithiocarbamate Metal Complexes and Their Electrochemical Behavior

Synthesis of Partially Graphitic Ordered Mesoporous Carbons with High Surface Areas

Preparation of Carbon-Coated Fe3O4 Porous Particles and Their Adsorption Properties of Iron (III) Ion

Synthesis of Carbon Encapsulated Magnetic Nanoparticles with Giant Coercivity by a Spray Pyrolysis Approach.