Mechanical Properties and Microstructures of Al2O3–5 Vol.% YAG Composites

HZ Wang,L Gao,ZJ Shen,M Nygren

DOI: https://doi.org/10.1016/s0955-2219(00)00262-4

IF: 5.7

2001-01-01

Journal of the European Ceramic Society

Abstract:Al2O3–5 vol.% YAG powder mixtures were prepared by three different methods: (i) Calcination of co-precipitated Al- and Y-hydroxides; (ii) precipitation of Al(OH)3 in a slurry containing nano-sized YAG particles, followed by calcination; (iii) ball milling of Al2O3 and YAG particles. Almost fully dense Al2O3–5 vol.% YAG compacts were obtained by hot-pressing these powders at a temperature equal to or exceeding 1550°C. Mechanical tests performed at room temperature showed that the bending strength of the Al2O3–5 vol.% YAG composite prepared from powder (i) was 604 MPa, and the fracture toughness 5.0 MPa m1/2, whereas compacts of the other two powders had lower bending strength and fracture toughness values. Microstructure investigations revealed a homogeneous distribution of YAG in the Al2O3 matrix in the compacts prepared from the powders (i) and (ii), although some nano-sized pores were found within the Al2O3 matrix prepared from powder (i).