Abstract:DSC, SEM–EDS, XRD and high-temperature XRD analysis was used to study thermal and crystallization behaviour of yttrium aluminate glasses prepared in the form of microspheres. The glasses YA-E (eutectic composition from the pseudo-binary system Al2O3–Y3Al5O12) and YA-G (a composition identical to the stoichiometric Y3Al5O12 (YAG) phase) were prepared by combination of the Pechini method with flame synthesis. The resulting microspheres were largely amorphous, but contained traces of yttrium–aluminium garnet as the main crystalline phase embedded in the yttrium aluminate glass matrix. Crystallization of the YAG phase was observed as the dominant exothermic process on DSC curves. From the DSC records, the basic thermal characteristics of the matrix glass, i.e. Tg (glass transition temperature), Tx (onset of crystallization peak temperature), Tf (temperature of the inflection point of the crystallization peak) and Tp (maximum of crystallization peak temperature), were determined. HT XRD experiments in the temperature interval 750–1200 °C and isothermal HT XRD experiments at 932, 998 and 1200 °C with 6-h holding time were also performed. Crystallization experiments at lower temperatures 932 °C (YA-E) and 915 °C (YA-G) were conducted to study phase development in a low-temperature region. Crystallization experiments at higher temperatures (1000, 1300 and 1500 °C) with maximum holding time of 6 h were performed to study crystallization of α-Al2O3 in the eutectic system. The SEM and SEM–EDS examination of polished cross sections of crystallized microspheres revealed slow volume crystallization of the YAG phase in the AY-E glass. Eventually, polycrystalline microspheres with fine-grained microstructure were prepared after 6-h treatment at 1500 °C.

PREPARATION AND MECHANICAL PROPERTIES OF POLYCRYSTALLINE YTTRIUM ALUMINUM GARNET

Preparation and Microstructure of Polycrystalline Al2O3–YAG Composites

Low‐Temperature Synthesis of Nanocrystalline Yttrium Aluminum Garnet Powder Using Triethanolamine

COMPARISON FOR PROPERTIES OF YTTRIUM ALUMINUM GARNET NANO-SIZED POWDER PREPARED BY DIFFERENT METHODS

Preparation of YAG Nanoparticles by Sol-Gel and Their Application in Electrical Contact Material

Preparation, Microstructure and Properties of Ternary Al2O3/YAG/ZrO2 Ceramics Hot Pressed with Eutectic Composition Powders

Mechanical Properties and Microstructures of Al2O3–5 Vol.% YAG Composites

Nanoscaled YAG Powders Via Coprecipitation Using Ammonium Hydrogen Carbonate As the Precipitant

Synthesis of nanoscaled yttrium aluminum garnet powder by the co-precipitation method

Synthesis of Nd3+ Doped Nano-Crystalline Yttrium Aluminum Garnet (YAG) Powders Leading to Transparent Ceramic

SYNTHESIS AND CHARACTERISTICS OF NEODYMIUM AND YTTERBIUM-DOPED YTTRIUM ALUMINUM GARNET NANO-POWDERS

Preparation and Characterization of Y3Al5O12:Nd Phosphor Powders by Ultrasonic Atomization and Co-precipitation Process

Rapid synthesis of Y3Al5O12 powders via plasma electrolysis

Phase composition, microstructure, and microwave dielectric properties of non-stoichiometric yttrium aluminum garnet ceramics

Co-precipitation processed needle-like YAG dispersed in alumina powder

Investigation Of High-Energy Ball Milling Of Al-Y2o3 Mixtures And Solid-State Reaction Synthesis Of Yag Ceramics

Preparation of Transparent YAG Ceramics via a Modified Solid-State Reaction Method

Solid Phase Synthesis and Sintering Properties of Yttrium Iron Garnet

Synthesis of Ytterbium-Doped Yttrium Aluminum Garnet Laser Ceramic Nano-Powders by Carbonate Altogether Precipitation Method

Mechanical properties of directionally solidified Al 2 O 3 /Y 3 Al 5 O 12 eutectic ceramic prepared by optical floating zone technique

Thermal behaviour of yttrium aluminate glasses studied by DSC, high-temperature X-ray diffraction, SEM and SEM–EDS