Waterborne polyurethane with high solid content synthesized by solvent-free

Ye Jiacan,Zhou Haifeng,Xu Wenlie,Liang Hui,Lai Shaomei,Lu Jiang

DOI: https://doi.org/10.3969/j.issn.1004-2849.2011.11.003

2011-01-01

Abstract:With mixed diisocyanate[hexamethylene diisocyanate(HDI)/isophorone diisocyanate(IPDI)] and polybutylene glycol adipate(PBA-2000) as basic raw materials,dimethylolbutyric acid(DMBA) as a hydrophilic monomer[instead of common dimethylolpropionic acid(DMPA)],triethylamine(TEA) as a neutralizer and ethylenediamine(EDA) as a chain extender,a waterborne polyurethane(WPU) with about 50% solid content and without organic solvent and catalyst was prepared by emulsifing prepolymer before chain extension.The better process conditions of preparing WPU emulsion were preferred by single-factor experiment.The results showed that the strength(tensile strength by 23 MPa) and toughness(elongation at break by 740%) were all better for WPU film when mass fraction of DMBA was 4.1%,molar ratios of n(-NCO)∶n(-OH) and n(EDA)∶n(-NCO) were 1.88∶1 and 0.37∶1 respectively.