Research on the ageing resistance of zirconia

Zhang Guoqiang,Wang Yan,Tian Jiemo,w C

DOI: https://doi.org/10.3969/j.issn.1672-5972.2011.01.001

2011-01-01

Abstract:Objective To evaluate the aging resistance of the new nano-zirconia composite ceramic.Methods Prepare the nano-zirconia composite ceramic samples and pure nano-zirconia ceramic samples from the nano-zirconia ceramic powder mixed up 5wt% alumina(TZ-3YS+5 wt% Al2O3) and the nano-zirconia ceramic powder(TZ-3YS),respectively,by the technique of cold isostatic pressing(CIP) and high temperature sintering(HTS).Boil 2 groups of samples up to 30 hours at the temperatures of 132 degrees and the pressure of 2 bars.And then,bend strength test,structure analysis of phases and observation of surface microstructure using scanning electron microscopy(SEM) are done in 2 groups of nano-zirconia ceramic samples.Results After the ageing,the bend strength by 345MPa(34.5%) in TZ-3YS and 154MPa(16.4%) in TZ-3YS+5 wt% Al2O3.Statistically,the difference between the decreases of the bend strength of 2 groups has significance(P < 0.05).The proportion of m-ZrO2 increased in 2 groups,but the amount of increase of m-ZrO2 in TZ-3YS is more than TZ-3YS+5 wt% Al2O3(P < 0.05).Conclusion The new nano-zirconia composite ceramic with 5wt% alumina is superior to the pure nano-zirconia ceramic in the mechanical stability and inner crystal composition after aging treatment.