Hydrothermal synthesis of mixed zinc–cobalt ferrite nanoparticles: structural and magnetic properties
P. Coppola,F. G. da Silva,G. Gomide,F. L. O. Paula,A. F. C. Campos,R. Perzynski,C. Kern,J. Depeyrot,R. Aquino
DOI: https://doi.org/10.1007/s11051-016-3430-1
IF: 2.533
2016-05-01
Journal of Nanoparticle Research
Abstract:We synthesize Zn-substituted cobalt ferrite (ZnxCo1−xFe2O4, with 0 ≤ x ≤ 1) magnetic nanoparticles by a hydrothermal co-precipitation method in alkaline medium. The chemical composition is evaluated by atomic absorption spectroscopy and energy-dispersive X-ray spectroscopy techniques. The structure and morphology of the nanopaticles are investigated by X-ray diffraction (XRD) and transmission electron microscopy (TEM), respectively. XRD Rietveld refinements reveal the cation distribution among the tetrahedral (A) and octahedral (B) sites. It shows that up to x ~0.5 zinc ions occupy preferably A-sites, above which Zn ions begin also a gradual occupancy of B-sites. TEM images show nanoparticles with different shapes varying from spheres, cubes, to octahedrons. Hysteresis loop properties are studied at 300 and 5 K. These properties are strongly influenced by the Zn and Co proportion in the nanoparticle composition. At 300 K, only samples with high Co content present hysteresis. At 5 K, the reduced remanent magnetization ratio (MR/MS) and the coercivity (HC) suggest that nanoparticles with x < 0.5 have cubic anisotropy. A kink on the hysteresis loop, close to the remanence, is observed at low temperature. This feature is presumably associated to interplay between hard and soft anisotropy regimes in the powder samples.Graphical Abstract
materials science, multidisciplinary,nanoscience & nanotechnology,chemistry