Abstract:Designing a novel microstructure with higher strength-ductility than lamellar microstructure (LM), which has been considered the most valuable engineering application in the service temperature range, is desired for lightweight TiAl alloys. Our prior publication reported a three-phase tri-modal (T-T) structure for Ti-43.5Al-4Nb-1Mo-0.1B(.at%) with superior mechanical properties than LM at room temperature (Ref: Acta Mater. 225 (2022) 117585). However, its strength-ductility at working temperature has yet to be fully exploited. This work fills the much-needed gap. The qualitative and quantitative optimizations indicate that the T-T structure's yield strength increases first and then decreases with increasing pearlitic-like microstructure (PM, which consist of three-phase (α 2 , γ and β o phase) with clear orientation relationships that form in a lamellar/cellular manner) content while the ductility keeps rising. When the T-T structure contains ∼20% PMs, it exhibits a yield strength about 130 MPa higher than LM coupling with doubled ductility at 750 °C. PMs can induce a prominent twinning induced plasticity and dislocation jog dragging (TWIP&DJD) effect, resulting in better strength-ductility below 700°C; above this temperature, the TWIP&DJD effect significantly plasticizes the alloys. The higher strength of the T-T structure at 750 °C is caused by hetero-deformation-induced strengthening between LMs and PMs, which cannot be offset by the plasticizing caused by PM when the volume fraction of PMs is less than 50%. This study demonstrates that introducing an appropriate amount of plasticizing structures (similar to PM) with excellent work hardening capacity is a promising strategy for enhancing the strength-ductility synergy of TiAl and possibly other brittle materials.

Strength properties and enhanced plasticity of intermetallic TiAl(CrSi) alloys

Tensile properties and fracture toughness of TiAl alloys with controlled microstructures

The Mechanical Properties of Intermetallic Ni50−xTi50Alx Alloys (X=6,7,8,9)

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Improved Fracture Toughness of Polycrystalline Γ‐tial‐based Intermetallic Alloys with a Favorable Deformation Mechanism of Twinning

Evading the strength-ductility trade-off at room temperature and achieving ultrahigh plasticity at 800°C in a TiAl alloy

High-density Deformation Nanotwin Induced Significant Improvement in the Plasticity of Polycrystalline Γ-Tial-based Intermetallic Alloys.

Breaking the high-temperature strength-ductility trade-off in TiAl alloys through microstructural optimization

Remarkable Improvement in Tensile Strength of a Polycrystalline Γ-Tial-based Intermetallic Alloy by Deformation Nanotwins

High-Density Deformation Nanotwin Further Improved Tensile Strength of Polycrystalline Γ-Tial-based Intermetallic Alloy

Recent Developments in Engineering Γ-Tial Intermetallics

A Preliminary Research on the Mechanical Properties of TiAl+Ti5Si3 Dual Phase Alloys

The Role of In-Situ Al3Ti Formed During Solidification in Improving the High-Temperature Properties of Al-Cu Alloy

High-strength and tunable plasticity in sputtered Al–Cr alloys with multistage phase transformations

Microstructure Evolution and Mechanical Properties of PM-Ti43Al9V0.3Y Alloy

Simultaneously Improved the Strength and Ductility of Cast Al-3Li-2Cu Alloy by Ti Addition and Heat Treatment

Solidification Microstructure Evolution and Mechanical Properties of Casting Ti-48Al-2Cr-2Nb-(Ni,TiB2)Alloy

Hierarchically heterogeneous strategy for Ti 2 AlC/TiAl composite with superior mechanical properties

The Influence of Microstructure on Superplastic Behaviours of Γ-Tial Alloys

Compositional and Microstructural Optimization and Mechanical-Property Enhancement of Cast Ti Alloys Based on Ti-6Al-4V Alloy

Microstructure Evolution in TiAl Alloyed with Si