Abstract:Suspension effect poses a big threat to the integrity and safety of corroded pipelines. In this work, a finite element (FE) based multi-physics field coupling model was developed to determine the mechano-electrochemical (M-E) interaction at an external corrosion defect on a suspended X100 steel pipe and predict its failure pressure. Theoretical calculations were used for model validation. Parameter effects including the defect location on the pipe, geometry of the defect, suspension length and pipe burial depth were determined. Results demonstared that, generally, the M-E effect at corrosion defect caused an increased stress concentration and anodic current density (i.e., corrosion rate), decreasing the failure pressure of the pipeline. The effect became more apparent when the pipe was in suspension. Both the stress and the anodic current density at the corrosion defect were dependent on the defect geometry, especially the defect depth. When the depth was up to 40% of pipe wall thickness, the von Mises stress exceeded the yield stress of the steel, causing local plastic deformation. A critical defect length of <math>20Dt</math> (D is the outer diameter of the pipe and t is pipe wall thickness) existed, below which the von Mises stress and the anodic current density at the corrosion defect increased with increased defect length. When the defect length exceeded the critical value, the effect was not obvious. An increased suspension length of the pipe would elevate the local stress and anodic current density at the corrosion defect, reducing the failure pressure of the pipe. A critical pipe burial depth of 2.5 m was identified, exceeding which the failure pressure of the pipe decreased rapidly with the increased burial depth. When the burial depth was smaller than 2.5 m, the effect was marginal. The location of the corrosion defect on the pipe did not affect the local stress, anodic current density and failure pressure at an appreciable level, and could be ignored in defect assessment on suspended pipelines.

Modified expression for estimating the limit bending moment of local corroded pipeline

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Assessment of Bending Resistance of Defected J55 Pipeline

A study of the ultimate compressive strain of local buckling in strain-based design of pipelines

Bending Resistance of Pipes with Local Defects

Plastic Limit Load Analysis for Pressure Pipe with Incomplete Welding Defects Based on the Extended Net Section Collapse Criteria

Bending failure of the corroded pipeline subjected to initial internal pressure and axial compressive force

Finite element analysis of the limit load of pipe bend with local wall-thinning defect under complex loads

Bending Capacity of Corroded Pipeline Subjected to Internal Pressure and Axial Loadings

Limit bending moment for pipes with two circumferential flaws under combined internal pressure and bending

Plastic Limit Load Analysis of Pressure Pipes Containing Incomplete Welding Defects under Combined Loadings

A novel strain-based assessment method of compressive buckling of X80 corroded pipelines subjected to bending moment load

Finite element modeling of local corrosion accelerated by the mechano-electrochemical coupling effect at defects on pipelines under combined effects of internal pressure and axial applied stress

Failure pressure analysis of corroded moderate-to-high strength pipelines

Assessment by finite element modelling of the mechano-electrochemical interaction at corrosion defect on elbows of oil/gas pipelines

Collapse Capacity of Corroded Pipes under Combined Pressure, Longitudinal Force and Bending

Time-dependent Reliability Assessment of Steel Pipelines Subjected to Localized Corrosion

Analytical prediction of failure pressure for pipeline with long corrosion defect

Modeling of mechano-electrochemical interaction at a corrosion defect on a suspended gas pipeline and the failure pressure prediction

Buckling response of subsea pipeline with irregular corrosion defect under external pressure

Failure Bending Moment for Pipes with an Arbitrary-Shaped Circumferential Flaw