Performance of a ceramic membrane reactor with high oxygen flux Ta-containing perovskite for the partial oxidation of methane to syngas
Huixia Luo,Yanying Wei,Heqing Jiang,Wenhui Yuan,Yangxiao Lv,Jürgen Caro,Haihui Wang
DOI: https://doi.org/10.1016/j.memsci.2009.12.023
IF: 9.5
2010-01-01
Journal of Membrane Science
Abstract:A novel dense BaCo0.7Fe0.2Ta0.1O3−δ (BCFT) perovskite membrane was successfully synthesized from BaCO3, Co2O3, Fe2O3 and Ta2O5 by a simple solid state reaction. X-ray diffraction (XRD) was used to characterize the phase formation process of BCFT precursors after ball-milling 24h in ethanol and calcining at different temperatures. The oxygen permeation under different driving forces shows that the oxygen permeation under an air/He oxygen gradient is controlled by bulk diffusion at 900°C for a membrane thickness from 0.6mm to 1.2mm. However, the oxygen permeation under the stronger oxygen gradient in the partial oxidation of methane (POM) to syngas reaction at 900°C is limited by the oxygen surface exchange. The POM to syngas in the BCFT reactor was successfully performed. Methane conversion was found to be >99% with 94% CO selectivity and 16.2ml/mincm2 oxygen permeation flux under a steady state condition was obtained at 900°C. Moreover, the BCFT membrane reactor has been steadily operated in the POM to syngas reaction for more than 400h without any fractures.