Growth, Structure and Thermal Properties of Yb3+-doped NaGd(WO4)2 Crystal

JD Fan,HJ Zhang,JY Wang,ZC Ling,HR Xia,XF Chen,YG Yu,QM Lu,MH Jiang
DOI: https://doi.org/10.1088/0022-3727/39/6/007
2006-01-01
Journal of Physics D Applied Physics
Abstract:Yb3+:NaGd(WO4)(2) single crystal with dimensions circle divide 30x60mm(2) has been grown by the Czochralski method. XRPD experimental results show that the as-grown Yb-3 +/-:NaGd(WO4)(2) crystal belongs to the tetragonal system and the I4(1)/a space group. The high crystalline quality of the as-grown Yb3+:NaGd(WO4)(2) crystals was confirmed by HRXRD. The effective segregation coefficient of the Yb element in Yb3+:NaGd(WO4)(2) crystal growth was measured to be 0.812 using the x-ray fluorescence method. Subsequently, the thermal properties were systematically studied by measuring the thermal expansion, specific heat and thermal diffusion coefficients. The density of the as-grown Yb3+:NaGd(WO4)(2) crystal at 22 degrees C was measured by using the buoyancy method with a resulting value of 7.143 g cm(-3) and almost linearly decreases as the temperature increases due to the thermal expansion. Comparing, the thermal properties of several tungstate crystals, we find that the Yb3+:NaGd(WO4)(2) crystal possesses relatively larger anisotropic thermal expansion and specific heat but smaller thermal conductivity than those of other tungstate crystals.
What problem does this paper attempt to address?