Growth, Structural, Thermal, and Optical Properties of a GaNbO4 Single Crystal

Yuzhen Li,Wenwen Huang,Ximeng Gu,Yiming Wang,Junqi Zhang,Hong Chen,Shiyi Guo

DOI: https://doi.org/10.1039/d2ce01163h

IF: 3.756

2022-01-01

CrystEngComm

Abstract:A high quality crystal of GaNbO4 was successfully grown for the first time by the Czochralski method, and the thermal and optical properties were systematically studied.

What problem does this paper attempt to address?

Growth, Structure, Spectral Properties and Crystal-Field Analysis of Monoclinic Nd:Ynbo4 Single Crystal

Shoujun Ding,Qingli Zhang,Jinyun Gao,Wenpeng Liu,Jianqiao Luo,Dunlu Sun,Guihua Sun,Xiaofei Wang

DOI: https://doi.org/10.1016/j.physb.2016.09.021

2016-01-01

Abstract:A Nd:YNbO4 single crystal was successfully grown by Czochralski (Cz) method, its structural and spectroscopic properties were investigated. The X-ray rocking curve of the (010) diffraction face of Nd:YNbO4 crystal was measured, the full width at half maximum (FWHM) of this diffraction peak is 0.05°, which indicates a high crystalline quality of the as-grown crystal. Its lattice parameters, atomic coordinates and so on were obtained by Rietvield refinement to X-ray diffraction data. According to the Archimedes drainage method, the crystal density of Nd:YNbO4 is calculated to be 5.4g/cm3. The Mohr′s hardness value along (010) face was determined to be 6.0. The transmission spectrum along (010) face at room temperature was recorded and the excitation and emission spectra at 8K were measured. Photoluminescence peaks of Nd:YNbO4 were assigned, and the crystal-field splitting of Nd3+ in YNbO4 was obtained. The fluorescence lifetime of the 4F3/2→4I11/2 transition of Nd3+ in YNbO4 is fitted to be 152μs These spectroscopic and energy splitting data give an important reference for the research of laser property of Nd:YNbO4 crystal.
High Quality (Innb)(0.1)Ti0.9o2 Single Crystal Grown Using Optical Floating Zone Method

Ziyi Liu,Yongli Song,Xianjie Wang,Yantao Su,Zhiguo Liu,Yu Sui

DOI: https://doi.org/10.1016/j.jcrysgro.2016.04.019

IF: 1.8

2016-01-01

Journal of Crystal Growth

Abstract:A crack-free (InNb)(0.1)Ti0.9O2 single crystal of 4 mm in diameter and 30 mm in length was successfully grown by the optical floating zone method. The polycrystalline feed and seed rods for growing the (InNb)(0.1)Ti0.9O2 single crystal were prepared by solid-state reaction method. The oxygen partial pressure significantly affected the crystal quality of the material. As shown in reflecting polarizing microphotographs, crystals grown in air have fewer grain boundaries than those grown in pure oxygen; some air-grown crystals are completely free of grain boundaries. Compared to pure TiO2 crystal, the (Nb+In) co-doped TiO2 crystal required a lower growth rate of 5 mm/h to ensure high quality. (C) 2016 Elsevier B.V. All rights reserved.
Floating zone growth and optical phonon behavior of corundum Mg4Ta2O9 single crystals

liang li,wenqiang liu,bo han,xilian jin,fangfei li,wenquan wang,qiang zhou,dapeng xu,tian cui

DOI: https://doi.org/10.1039/c5ra12071c

IF: 4.036

2015-01-01

RSC Advances

Abstract:We demonstrate that corundum Mg4Ta2O9 crystals, free of low-angle grain boundaries and bubbles, were prepared for the first time by the infrared heating optical floating zone method. The X-ray diffraction results showed that the crystals had corundum structure, cleaved parallel to the c plane and grew along the a-axis. The temperature-dependent optical phonon behavior of Mg4Ta2O9 were also investigated in the range from 84 to 834 K.
Optical Floating Zone Method Growth and Optical Properties of Corundum Mg4nb2o9 Single Crystal

Liang Li,Defang Duan,Qiang Zhou,Dapeng Xu,Tian Cui,Bingbing Liu,Hongming Yuan

DOI: https://doi.org/10.1016/j.jcrysgro.2014.05.006

IF: 1.8

2014-01-01

Journal of Crystal Growth

Abstract:Mg4Nb2O9 single crystals were prepared by the optical floating zone method. While the as-grown were boules polycrystalline and cracked with dimensions of ∅ 5–8mm×L 91mm, they contained single crystal regions as large as ∅ 4mm×L 15mm. The X-ray diffraction analysis showed that the crystals had the corundum structure, grew along the a-axis and cleaved parallel to the c plane. Polarized light microscopy, in a cross-transmission configuration measurement, showed that the crystal was free of low-angle grain boundaries and bubbles. The optical interband transitions were measured from the absorption spectrum of the crystal along the c-axes at room temperature in the range of 200–800nm. Based on the theory of band-to-band transitions, the direct band gap was determined for the first time to be Eg=5.09eV. The photoluminescence spectra exhibited a broad and strong blue emission band centered at 450nm.
Study of Crystal Growth and Characteristics of New Nonlinear Optical Crystal RCa4O(BO3)3(R=Gd,Y)

ZHANG Shujun,ZHANG Jiguo,CHENG Zhenxiang,ZHOU Guangyong,HAN Jianru,CHEN Huanchu

DOI: https://doi.org/10.3321/j.issn:1001-9731.2000.02.031

2000-01-01

Journal of Functional Biomaterials

Abstract:This paper reports the growth of large size,high quality GdCa 4O(BO 3) 3 (GCOB) and YCa 4O(BO 3) 3 (YCOB) crystals using Czochraski pulling method from platinum crucible under air atmosphere for the first time.The 〈010〉 was selected as the optimum growth direction by comparing several growth orientations.The growth habits were studied and the cause of the dendritic growth on the twin interface were discussed.The crystals were known to have broad transparency range and have high transmittance in the deep UV region by measuring their transmission spectra.They have good frequency-doubling function,we obtained 26.7% frequency-doubling conversion efficiency which performed on a 5mm GCOB crystal.GCOB and YCOB crystals also can be realized self-frequency-doubling by doping.
High-quality Single Crystal Growth and Spin Flop of Multiferroic Co4Nb2O9

Yiming Cao,Yali Yang,Maolin Xiang,Zhenjie Feng,Baojuan Kang,Jincang Zhang,Wei Ren,Shixun Cao

DOI: https://doi.org/10.1016/j.jcrysgro.2015.03.045

IF: 1.8

2015-01-01

Journal of Crystal Growth

Abstract:A single crystal of Co4Nb2O9 about 7mm in diameter and 55mm in length was successfully grown by an optical floating zone method. X-ray powder diffraction (XRD) indicates that it has a single phase corundum-type structure. Clear Laue spots and sharp XRD peaks confirm the good quality and crystallographic orientations. Below TN, magnetization of Co4Nb2O9 along a axis shows dramatically different behaviors between H=1kOe and 20kOe, suggesting a spin flop occurs along a axis. Ma(H) curve at 5K shows a change of slope at a critical magnetic field of 7.5kOe for triggering the spin flip.
Self-consistent Growth of Single-Crystalline (2̄01)Β-Ga2o3nanowires Using a Flexible GaN Seed Nanocrystal

Pengyu Song,Zhengyuan Wu,Xiyang Shen,Junyong Kang,Zhilai Fang,Tong-Yi Zhang

DOI: https://doi.org/10.1039/c6ce02319c

IF: 3.756

2017-01-01

CrystEngComm

Abstract:Single-crystalline (01)β-Ga2O3 nanowires were grown by using a flexible GaN seed nanocrystal "self-organizing" around catalytic Pt droplets. The atomic structures of β-Ga2O3(01) epitaxy on GaN(0001) were investigated by X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, Raman spectroscopy, and cathodoluminescence (CL). The synthesized nanowires prepared by self-consistent growth are single crystals of pure β-Ga2O3 phase with (01)-orientation and high crystalline quality and have intense ultraviolet–blue CL emission properties at room temperature.
Study on the Growth and Optical Activity of Sr3NbGa3Si2O14 Single Crystals

Z. Wang,D. Yuan,A. Wei,H. Qi,X. Shi,G. Zhang,D. Xu,M. Lü

DOI: https://doi.org/10.1007/s00339-003-2429-5

2004-01-01

Applied Physics A

Abstract:Crystals of Ca3NbGa3Si2O14 (CNGS) with ordered langasite structure were grown using the Czochralski method along the Cartesian X axis [110]. The as-grown crystals exhibit high optical quality and structure perfection. Optical activities were obtained by measuring polarised transmission at various wavelengths between crossed polarisers using a TU-1900 spectrophotometer and we found that CNGS crystals showed very large values of ϱ.
Crystal growth and design of Sn-doped β-Ga2O3: Morphology, defect and property studies of cylindrical crystal by EFG

Bo Fu,Guangzhong Jian,Wenxiang Mu,Yang Li,Huanyang Wang,Zhitai Jia,Yanbin Li,Shibing Long,Yujun Shi,Xutang Tao

DOI: https://doi.org/10.1016/j.jallcom.2021.162830

IF: 6.2

2022-03-01

Journal of Alloys and Compounds

Abstract:The cylindrical Sn: β-Ga2O3 crystal with high crystalline quality was successfully designed and grown by the innovative edge-defined film-fed growth (EFG) method equipped with a cylindrical Iridium die. The challenges for the growth of Sn: β-Ga2O3 crystals were overcome by optimizing the design of an afterheater. The growth morphology of cylindrical β-Ga2O3 crystal was studied using a theoretical model and the results from experimental crystal growth. The order of importance of growth conditions affecting β-Ga2O3 crystal growth morphology was examined, based on the morphological features of cylindrical β-Ga2O3 crystals obtained by the EFG and Czochralski methods. The iridium inclusions with three shapes were observed in bulk β-Ga2O3 crystal, and the formation mechanism was carefully discussed. The optical bandgap and valence band maximum (VBM) of Sn: β-Ga2O3 crystal were calculated to be 4.74 eV and 3.49 eV by absorption spectra and X-ray photoelectron spectroscopy (XPS), respectively. The corresponding surface barrier height (Φ surf ) was 1.25 eV. The carrier concentration of 5.95 × 1018 cm−3 was characterized by capacitance-voltage (C-V) measurement. By the Hall measurement, the carrier mobility and resistivity were estimated to be around 51 cm2 V−1 s−1 and 3.55 × 10–2 Ω cm, respectively.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
Crystal growth and properties of Nd : NaBi (WO4)(2)

J Sun,ZL Zhu,Y Gao,JH Liu,CR Yili

IF: 4.632

2003-01-01

Journal of Rare Earths

Abstract:Nd:NaBi(WO4)(2) crystals (Nd:NBW) were grown by Czochralski method. The pulling rate is 0.3 mm.h(-1), and the rotational speed of Nd:NBW crystal is 2 r.min(-1). The components of this single crystal were determined by X-ray diffractions, and its corresponding properties were described from thermal gravity and differential thermal analysis experiments. The absorption cross-sections were calculated. The emission band of Nd:NBW crystal was obtained from its luminous spectrum.
Basic Properties of A New Nd-Doped Laser Crystal: Nd: Gdnbo4

Shoujun Ding,Qingli Zhang,Wenpeng Liu,Jianqiao Luo,Dunlu Sun

DOI: https://doi.org/10.1007/s12200-017-0715-7

2017-01-01

Frontiers of Optoelectronics

Abstract:A Nd-doped GdNbO4 single crystals have been grown successfully using the Czochralski technique. The chemical etching method was employed to study the defects in the structural morphology of Nd:GdNbO4 crystal with phosphoric acid etchant. Mechanical properties (such as hardness, yield strength, fracture toughness, and brittle index) of the as-grown crystal were systematically estimated on the basis of the Vickers hardness test for the first time. The transmission spectrum of Nd:GdNbO4 was measured in the wavelength range of 320–2400 nm at room temperature, and the absorption peaks were assigned. Results hold great significance for further research on Nd:GdNbO4.
Growth, Structure, and Spectroscopic Properties of 5 At.% Yb:GdNbO4 Laser Crystal

Renqin Dou,Qingli Zhang,Jianqiao Luo,Jiakang Chen,Huajun Yang,Wenpeng Liu,Guihua Sun,Dunlu Sun

DOI: https://doi.org/10.1016/j.optmat.2014.12.018

IF: 3.754

2015-01-01

Optical Materials

Abstract:A new crystal of Yb-doped gadolinium niobate, 5 at.% Yb:GdNbO4, is grown by Czochralski method for the first time. The structure of Yb:GdNbO4 is determined by Rietveld refinement to the X-ray powder diffraction data and it belongs to the monoclinic space group of I-2/a. With the center of 955 nm, the FWHM of absorption spectra is 57 nm and the absorption cross section is calculated to be 0.97 x 10(-20) cm(2). Spectral parameters are calculated with absorption spectrum. In emission spectra, the strongest peak is at 1001 rim and the FWHM is 49 rim. In comparison with corresponding emission cross section of Yb:YSO and Yb:GSO, Yb:GdNbO4 exhibits a relatively larger emission cross section. In addition, a maximal output power of 270 mW is obtained and the slope efficiency is 7.5%. (C) 2015 Elsevier B.V. All rights reserved.
Study on the Growth of Lattice-matched ScAlMgO_4 Substrates for GaN and ZnO-based Film Epitaxy

TANG Hui-li,DONG Yong-jun,XU Jun,ZHAO Zhi-wei,WU Feng,ZOU Jun,ZHOU Guo-qing

DOI: https://doi.org/10.3969/j.issn.1000-985x.2007.03.028

2007-01-01

Abstract:A transparent white ScAlMgO4 crystal used as lattice-matched substrate for GaN and ZnO epitaxial film has been grown by Czochralski method.The as-grown crystal boules were about 30mm×59mm in dimension and cracked slightly along cleavage plane.With the XRD pattern of sintered raw analysis,it is confirmed that solid-state reaction sintering at 1400℃ ScAlMgO4 polycrystal phase preliminarily synthesized.Polarizing microscopy,XRD pattern,transmission spectrum and X-ray rocking curve characterization indicate the as-grown crystal is of fine crystalline and optical property.Studies show that the cracking phenomena of the ScAlMgO4 crystals occurred during the growth process are mainly originated from its intrinsic layer structure,relatively larger temperature gradient and inhomogeneity of thermal stress.
Crystal Growth, Optical, Thermal and Piezoelectric Properties of HoCa4O(BO3)3 Crystal

Pingzhang Yu,Xiaobo Pan,Guangda Wu,Yanqing Liu,Fapeng Yu,Zhengping Wang,Xinguang Xu

DOI: https://doi.org/10.1039/d1ce00816a

IF: 3.756

2021-01-01

CrystEngComm

Abstract:High-quality crystals of HoCa4O(BO3)3 were grown by the Czochralski method. The optical, thermal and piezoelectric properties were investigated.
2 in. Bulk β-Ga2O3 Single Crystals Grown by EFG Method with High Wafer-Scale Quality

Ganrong Feng,Shan Li,Yawen Tian,Song Qi,Daoyou Guo,Weihua Tang

DOI: https://doi.org/10.1021/acsomega.4c00405

IF: 4.1

2024-04-24

ACS Omega

Abstract:2 in. bulk β-Ga2O3 single crystals are successfully grown by the edge-defined film-fed growth method with a homemade furnace system. By considering the significance of wafer quality in future mass manufacture, a nine-point characterization method is developed to evaluate the full-scale quality of the processed 2 in. (100)-orientated β-Ga2O3 single-crystal wafers. Crystalline and structural characteristics were evaluated using X-ray diffraction and Raman spectroscopy, revealing decent crystalline quality with a mean full width at half-maximum value of 60.8 arcsec and homogeneous bonding structures. The statistical root-mean-square surface roughness, determined from nine scanning areas, was found to be only 0.196 nm, indicating superior surface quality. Linear optical properties and defect levels were further investigated using UV-visible spectrophotometry and photoluminescence spectroscopy. The high wafer-scale quality of the processed β-Ga2O3 wafers meets the requirements for homoepitaxial growth substrates in electronic and photonic devices with vertical configurations.
Thermal, defects, mechanical and spectral properties of Nd-doped GdNbO 4 laser crystal

Shoujun Ding,Qingli Zhang,Jianqiao Luo,Wenpeng Liu,Xiaofei Wang,Guihua Sun,Xiuli Li,Dunlu Sun

DOI: https://doi.org/10.1007/s00339-017-0928-z

2017-01-01

Applied Physics A

Abstract:A Nd-doped GdNbO 4 crystal was grown successfully by Czochralski method. Its monoclinic structure was determined by X-ray diffraction; the unit-cell parameters are a = 5.38 Å, b = 11.09 Å, c = 5.11 Å, and β = 94.56°. The morphological defects of Nd:GdNbO 4 crystal were investigated using the chemical etching with the phosphoric acid etchant. For a new crystal, the physical properties are of great importance. The hardness and density of Nd:GdNbO 4 were investigated first. Thermal properties of Nd:GdNbO 4 , including thermal expansion coefficient and specific heat, were measured along a-, b- , and c -crystalline axes. Thermal properties indicate that the Nd:GdNbO 4 pumped along c -axis can reduce the thermal lensing effect effectively. The specific heat is 0.53 J g −1 K −1 at 300 K, indicating a relatively high damage threshold of Nd:GdNbO 4 . The transmission and emission spectrum of Nd:GdNbO 4 were measured, and the absorption peaks were assigned. The strongest emission peak of Nd:GdNbO 4 is located at 1065.3 nm in the spectral range of 850–1420 nm excited by 808 nm laser. The refractive index of Nd:GdNbO 4 was calculated with the transmission spectrum and fitted with Sellmeier equation. All these obtained results is of great significance for the further research of Nd:GdNbO 4 .
Basic Properties of a New Nd-doped Laser Crystal: Nd:GdNbO4

Shoujun DING,Qingli ZHANG,Wenpeng LIU,Jianqiao LUO,Dunlu SUN

DOI: https://doi.org/10.1007/s12200-017-0715-7

2017-01-01

Frontiers of Optoelectronics

Abstract:A Nd-doped GdNbO4 single crystals have been grown successfully using the Czochralski technique. The chemical etching method was employed to study the defects in the structural morphology of Nd:GdNbO4 crystal with phosphoric acid etchant. Mechanical properties (such as hardness, yield strength, fracture toughness, and brittle index) of the as-grown crystal were systematically estimated on the basis of the Vickers hardness test for the first time. The transmission spectrum of Nd:GdNbO4 was measured in the wavelength range of 320–2400 nm at room temperature, and the absorption peaks were assigned. Results hold great significance for further research on Nd:GdNbO4.
Single Crystal Growth of CuFe1−Ga O2 by the Optical Floating-Zone Method

J. D. Song,J. C. Wu,X. Rao,S. J. Li,Z. Y. Zhao,X. G. Liu,X. Zhao,X. F. Sun

DOI: https://doi.org/10.1016/j.jcrysgro.2016.04.046

IF: 1.8

2016-01-01

Journal of Crystal Growth

Abstract:We report a systematic study on the crystal growth of CuFe1−xGaxO2 (x=0, 0.035, 0.08, and 0.12) by using an optical floating-zone method. High-quality single crystals are successfully obtained and the growth conditions are carefully optimized. It is found that there is a wide region to set the heat power for crystallizing, but the best crystallization requires carefully adjusting the heat power. X-ray diffraction data demonstrate the good crystallinity of these crystals. The basic physical properties of these crystals are characterized by the magnetic susceptibility and thermal conductivity measurements.
Single crystal growth of Mn4Nb2O9 and its structure-magnetic coupling

Yiming Cao,Maolin Xiang,Zhenjie Feng,Baojuan Kang,Jincang Zhang,Nicolas Guiblin,Wei Ren,Brahim Dkhil,Shixun Cao

DOI: https://doi.org/10.1039/c6ra26231g

IF: 4.036

2017-01-01

RSC Advances

Abstract:A single crystal of Mn4Nb2O9 of about 8 mm in diameter and 30 mm in length was successfully grown by a newly designed one-step method based on the optical floating zone technique. Clear Laue spots and sharp XRD Bragg reflections attest the good crystal quality. The antiferromagnetic phase transition at T-N = 108.4 K of the Mn4Nb2O9 single crystal was observed along the c axis, which contrasts with Co4Nb2O9 belonging to the same structural family. Structural changes with a-axis shrinkage and c-axis expansion at T-N demonstrate a significant and anisotropic magnetostriction effect.
Growth and properties of a new birefringent α-BaB2O4 crystal

Guoqing Zhou,Jun Xu,Xingda Chen,Heyu Zhong,Siting Wang,Ke Xu,Peizhen Deng,Fuxi Gan,

1998-01-01

Abstract:A novel birefringent α-BaB2O4 crystal with 40 mm in diameter, 35 mm in height has been grown successfully in our laboratory by Czochralski method. The proportion of B2O3 and BaO of starting material, crystal cracking and the transmission spectrum of α-BaB2O4 crystal have been briefly analyzed.

Growth, Structural, Thermal, and Optical Properties of a GaNbO4 Single Crystal

Growth, Structure, Spectral Properties and Crystal-Field Analysis of Monoclinic Nd:Ynbo4 Single Crystal

High Quality (Innb)(0.1)Ti0.9o2 Single Crystal Grown Using Optical Floating Zone Method

Floating zone growth and optical phonon behavior of corundum Mg4Ta2O9 single crystals

Optical Floating Zone Method Growth and Optical Properties of Corundum Mg4nb2o9 Single Crystal

Study of Crystal Growth and Characteristics of New Nonlinear Optical Crystal RCa4O(BO3)3(R=Gd,Y)

High-quality Single Crystal Growth and Spin Flop of Multiferroic Co4Nb2O9

Self-consistent Growth of Single-Crystalline (2̄01)Β-Ga2o3nanowires Using a Flexible GaN Seed Nanocrystal

Study on the Growth and Optical Activity of Sr3NbGa3Si2O14 Single Crystals

Crystal growth and design of Sn-doped β-Ga2O3: Morphology, defect and property studies of cylindrical crystal by EFG

Crystal growth and properties of Nd : NaBi (WO4)(2)

Basic Properties of A New Nd-Doped Laser Crystal: Nd: Gdnbo4

Growth, Structure, and Spectroscopic Properties of 5 At.% Yb:GdNbO4 Laser Crystal

Study on the Growth of Lattice-matched ScAlMgO_4 Substrates for GaN and ZnO-based Film Epitaxy

Crystal Growth, Optical, Thermal and Piezoelectric Properties of HoCa4O(BO3)3 Crystal

2 in. Bulk β-Ga2O3 Single Crystals Grown by EFG Method with High Wafer-Scale Quality

Thermal, defects, mechanical and spectral properties of Nd-doped GdNbO 4 laser crystal

Basic Properties of a New Nd-doped Laser Crystal: Nd:GdNbO4

Single Crystal Growth of CuFe1−Ga O2 by the Optical Floating-Zone Method

Single crystal growth of Mn4Nb2O9 and its structure-magnetic coupling

Growth and properties of a new birefringent α-BaB2O4 crystal