Abstract:By employing modified top-seeded melt growth, a sizable Y1-xCaxBa2Cu3Oy (Ca-YBCO) crystal (16 mm in diameter) with a high doping level was grown for the first time. The crystal is a substance of remarkable importance in the study of superconductivity, distinctively by neutron scattering experiments. Firstly, our findings show that the addition of CaCO3 to the precursors significantly changes the liquid properties, leading to serious liquid loss. In consequence, as-grown samples are unexpectedly characterized by an incomplete growth and a high density of the Y211 phase. Furthermore, a series of experiments have been conducted to improve growth conditions. Our results prove that by using a novel sample construction, setting thin pellets underneath and on top of the main pellet as a liquid reservoir, the aforementioned problems can be effectively solved. As a result, a fully-grown Ca-YBCO crystal with less Y211 particles was achieved.

High-Tc Superconductivity In Yba2cu3o7-Y, Gdba2cu3o7-Y, Ybba2cu3o7-Y Single-Crystal With Large Size

High Tc superconductivity in LnBa2Cu3O7−y(Ln=Y, Gd, Dy, Yb) single crystal with large size

High T C Superconductivity in LnBa 2 Cu 3 O 7- Y (ln=yb, Er) Single Crystal with Large Size

THE GROWTH OF LARGE SINGLE CRYSTAL OF LnBa2Cu3O7-δ AND THEIR SUPERCONDUCTIVITY

High Tc Superconductivity in Single Crystal YBa2Cu3O7−δ

A Method for Preparing Superconducting Single Crystals of Ba2GdCu3O7−y

Structure of the High-Tcsuperconductorba2

Research on anisotropy for single crystal GdBa2Cu3O7−y

Growth and properties of superconducting YBCO single crystals

The Crystal Structure and Ordering of Nb5+ Doped High Tc Superconductors Ba3−yYyCu3−xNbxO9−z

Antiferromagnetic Ordering in the High-Tc Superconductors (y1−xgdx) Ba2Cu3O7−y

Superconducting Oxide Dy-Ba-Cu-O with TC(π=0) Beyond 90K

Structure of the High-Tcsuperconductorba2y<…

The Crystal Structure of BaY2O4, Isotypic with SrY2O4

Superconductivity of (tl 1-X Al X ) 2 Ba 2 Ca 2 Cu 3 O Y

A new phase with tetragonal structure in the GdBaCuClO system

CBED AND SAED STUDY OF HIGH Tc Ba-Y-Cu-O SUPERCONDUCTORS

Modified top-seeded melt growth for large sized Y1−xCaxBa2Cu3Oy crystals

Superconductivity And Thermal-Stability Of The Yba2cu3-Xznxo7-Y System

Crystal Growth Mechanism of Ybco Superconductors Prepared by Unidirectional Solidification Method

Growth, Characterization and Physical Properties of High-Quality Large Single Crystals of Bi2(Sr2−xLax)CuO6+δhigh-temperature Superconductors