The Growth and Properties of Rare Earth-Doped NaY(WO4)2 Large Size Crystals
Chaoyang Tu,ZhenYu You,Jianfu Li,Yan Wang,Zhaojie Zhu
DOI: https://doi.org/10.5772/28716
2012-01-01
Abstract:Recently, strong attention has been focused on development of a new-advanced material for optoelectronics applications. MRe(WO4)2 [M=alkali metal, Re=rare earth] single crystals is noticed as an interesting self-frequency conversion solid-state laser host material because of stimulated Raman scattering[1]. NaY(WO4)2 crystal is classified among the disorder crystalline host for lasing rare-earth ions[2]. Because of the disorder structure, the optical features in the absorption and emission spectrum even at low temperature are broadened. The lattice parameters of NaY(WO4)2 crystal are a=b=5.205 Å and c=11.251 Å respectively with the space group of I41/a [3]. This crystal is a typical tetragonal scheelite-type crystal with a formula MT(WO4)2 , where M is a monovalent alkali cation and T a trivalent cation . In these materials the M and T cations are randomly distributed in the 2b and 2d sites [4], which can be replaced by rare earth ions, such as Nd3+, Yb3+, Tm3+, Ho3+ and Ce3+. As a consequence, the optical absorption and emission lines of rare earth doping ions become broadened, which allow some laser tunability as well as a better match with the available diode laser emissions used for pumping. As it melts congruently, large size single crystal can be easily obtained by the Czochralski (CZ) method. Furthermore, the higher concentration of rare earth ions can be accepted in the crystal because of the higher covalent characteristic results in the lower luminescent quenching efficiency. Compared to the other laser host crystals such as YAG and YVO4 crystal, NaY(WO4)2 crystal has lower melting point and its raw materials for crystal growth is in-nocuity. As a result, NaY(WO4)2 crystal can serve as an excellent laser host. In this chapter, the crystal growth, thermal characteristic, optical and spectrum and laser properties of rare earth dopedNaY(WO4)2 crystals are presented.