Crystal Growth and Spectrum Properties of Nd3+:Er3+:KY(WO4)2

涂朝阳,李坚富,朱昭捷,王燕,游振宇,吴柏昌

DOI: https://doi.org/10.3321/j.issn:1000-0593.2003.04.013

2003-01-01

Abstract:Crystal of Nd 3+ :Er 3+ :KY(WO_4)_2 with dimensions of up to 45 mm and good quality was grown from KWO_4 solvent by using the flux method. From the crystal boule grown, a high quality laser crystal rod of up to 3 mm in diameter and 11.9 mm in length was cut out. Absorption spectrum of this crystal ranging from violet to infrared was measured. It shows that there are nine absorption bands belonging to Nd 3+ and Er 3+ ions: 974.88 nm; 801.0(798.12, 803.95)nm; 748.5(753.5, 743.49)nm; 653.61nm; 586.65 nm; 518.6(545.03, 521.32, 489.35) nm; 452.80 nm; 407.81 nm and 367.22(377.24, 366.4, 358.02) nm. According to the energy transitions of Nd 3+ and Er 3+ ions, nine absorption bands have been confirmed. Meanwhile, the fluorescence spectrum of this crystal at room temperature was measured by using Edinburgh-Instrument F920 spectrometer. The result of the study shows that the co-doping Nd 3+ ions can enhance the absorption of this crystal at 800 nm emitted by AlGaAs laser diode.