Abstract:In this work, Chemical Vapour Deposition (CVD) has been used to synthesize boron nitride (BN) nanostructures, particularly nanotubes, and selectively introduce defects into the lattice of the synthesized BN nanostructures through ion implantation. Scanning electron microscopy (SEM) images show clear evidence of BN nanostructures and BN nanotubes (BNNTs), with the latter appearing as long, thin structures with diameters ranging from ⁓30-80 nm. Raman analysis show an E2g mode of vibration assigned to hexagonal BN (h-BN) at 1366 cm-1 after ion implantation, with increased intensity. Grazing incidence X-ray diffraction (GIXRD) spectra revealed a prominent peak between 54 and 56°, corresponding to the (004) h-BN reflection, which was used to determine the average lattice parameter c⁓0.662 nm representing the stacking direction of the BN layers. The majority of the samples had broad peaks, indicative of a nanocrystalline material. The only exception was the sample grown at 1200 °C, which was found to have a Scherrer crystallite size >100 nm. In contrast, the rest of the samples had an average size of 3.5 nm. Notable observations in this study include a significant rise in the size of the Raman derived crystallite domains in the nanostructures synthesized at 1100 and 1200 °C after ion implantation with boron ions at fluence 5 × 1014 ions/cm2.

Investigating the Structure of Boron Nitride Nanotubes by Near-Edge X-ray Absorption Fine Structure (NEXAFS) Spectroscopy

Near-Edge X-Ray Absorption Fine Structure Spectroscopy As A Tool for Investigating Nanomaterials

Fine Structure of Boron Nitride Nanotubes Produced from Carbon Nanotubes by A Substitution Reaction

X-ray Excited Optical Luminescence from Hexagonal Boron Nitride Nanotubes: Electronic Structures and the Role of Oxygen Impurities.

Structural systematics in boron-doped single wall carbon nanotubes

Deformation and Bifurcation Analysis of Boron-Nitride Nanotubes

Raman Spectroscopy of Single-Wall Boron Nitride Nanotubes

A XANES characterization of structural defects in single-walled carbon nanotubes

The Excitonic Effects In Single And Double-Walled Boron Nitride Nanotubes

Structural characterizations and electronic properties of boron nitride nanotube crystalline bundles.

Internal nanostructure diagnosis with hyperbolic phonon polaritons in hexagonal boron nitride

Study of the phase nature of boron- and nitrogen-containing films by optical and photoelectron spectroscopy

Synthesis and Modification of Boron Nitride nanotubes using ion implantation

The structure and local chemical properties of boron-terminated tetravacancies in hexagonal boron-nitride

Formation and Structure of Boron Nitride Conical Nanotubes

Recent Advances in Boron Nitride Nanotubes and Nanosheets

Structure of Boron Nitride Nanoscale Cones: Ordered Stacking Of240°and300°disclinations

Investigation on the Electronic Structure of BN Nanosheets Synthesized Via Carbon-Substitution Reaction: the Arrangement of B, N, C and O Atoms.

Raman Spectroscopy and Time-Resolved Photoluminescence of BN and BxCyNz Nanotubes

Unveiling the atomic structure of single-wall boron nanotubes

High-resolution surface structure determination from bulk X-ray diffraction data