Abstract:Advanced high-strength steels (AHSS) have a wide range of applications in equipment safety and lightweight design, and enhancing the strength of AHSS to the ultra-high level of 2 GPa is currently a key focus. In this study, a new process of thermo-mechanical control process followed by direct quenching and partitioning (TMCP-DQP) was developed based on Fe-0.4C-1Mn-0.6Si (wt.%) low-alloy steel, and the effects of microstructure evolution on mechanical properties under TMCP-DQP process and conventional hot rolled quenched and tempered process (HR-QT) were comparatively studied. The results show that the TMCP-DQP process not only shortened the processing steps but also achieved outstanding comprehensive mechanical properties. The TMCP-DQP steel exhibited a tensile strength of 2.23 GPa, accompanied by 11.9% elongation and a Brinell hardness of 624 HBW, with an impact toughness of 28.5 J at −20 °C. In contrast, the HR-QT steel exhibited tensile strengths ranging from 2.16 GPa to 1.7 GPa and elongations between 5.2% and 12.2%. The microstructure of TMCP-DQP steel primarily consisted of lath martensite, containing thin-film retained austenite (RA), nanoscale rod-shaped carbides, and a minor number of nanoscale twins. The volume fraction of RA reached 7.7%, with an average carbon content of 7.1 at.% measured by three-dimensional atom probe tomography (3DAP). Compared with the HR-QT process, the TMCP-DQP process resulted in a finer microstructure, with a prior austenite grain (PAG) size of 11.91 μm, forming packets and blocks with widths of 5.12 μm and 1.63 μm. The TMCP-DQP process achieved the ultra-high strength of low-alloy steel through the synergistic effects of grain refinement, dislocation strengthening, and precipitation strengthening. The dynamic partitioning stage stabilized the RA through carbon enrichment, while the relaxation stage reduced a small portion of the dislocations generated by thermal deformation, and the self-tempering stage eliminated internal stresses, all guaranteeing considerable ductility and toughness. The TMCP-DQP process may offer a means for industries to streamline their manufacturing processes and provide a technological reference for producing 2.2 GPa grade AHSS.

An Ultrahigh Strength Steel Produced Through Deformation-Induced Ferrite Transformation and Q&P Process

Ultrahigh strength-ductility steel treated by a novel quenching–partitioning–tempering process

The Microstructural design and control of ultrahigh strength-ductility martensitic steels based on a novel quenching-partitioning-tempering process

Study of a Novel Ultra-High Strength Steel with Adequate Ductility and Toughness by Quenching-Partitioning-Tempering Process

The Mechanism of High Strength-Ductility Steel Produced by A Novel Quenching-Partitioning-Tempering Process and the Mechanical Stability of Retained Austenite at Elevated Temperatures

Novel Ultrahigh-Strength Nanolath Martensitic Steel by Quenching–partitioning–tempering Process

High Strength Ductility Steels Treated by Novel Quenching–partitioning–tempering Process

Ultra-high Strength Steel Treated by Using Quenching–Partitioning–Tempering Process

The investigation of ultra-high strength steel by quenching-partitioning- tempering (Q-P-T) process

Enhancing Strength and Plasticity Synergy in Transformation-Induced Plasticity-Aided Lean Duplex Stainless Steel Based on the Ultrafine-Grained Austenite

A novel microstructural design and heat treatment technique based on gradient control of carbon partitioning between austenite and martensite for high strength steels

A Carbide-Free Bainite/martensite/austenite Triplex Steel with Enhanced Mechanical Properties Treated by a Novel Quenching–partitioning–tempering Process

An ultrahigh strength steel with ultrafine-grained microstructure produced through intercritical deformation and partitioning process

The Fabrication of Ultrahigh-Strength Steel with a Nanolath Structure via Quenching-Partitioning-Tempering

Room-Temperature Quenching and Partitioning Steel

Quenching-Partitioning-Tempering(Precipitation)(Q-P-T) Process for Ultra-high Strength Steel

Transformation-Induced Ductility of Reverse Austenite Evolved by Low-Temperature Tempering of Martensite

Achieving 2.2 GPa Ultra-High Strength in Low-Alloy Steel Using a Direct Quenching and Partitioning Process

Effects of Novel Q-P-T and Traditional Q-T Processes on the Microstructure and Mechanical Properties of Martensitic Steels with Different Carbon Content

The Principle and Mechanism of Enhancement of Both Strength and Ductility of Martensitic Steels by Carbon

A New Effect of Retained Austenite on Ductility Enhancement of Low Carbon Q-P-T Steel