Transformation-Induced Ductility of Reverse Austenite Evolved by Low-Temperature Tempering of Martensite

Pengju Du,Peng Chen,Devesh K. Misra,Di Wu,Hongliang Yi
DOI: https://doi.org/10.3390/met10101343
IF: 2.695
2020-10-07
Metals
Abstract:A novel steel combining the “quenching and tempering (Q&T)” process was exploited that can achieve the enhancement of austenite by interface migration during tempering the martensitic matrix mixed with films of austenite. A high uniform elongation (12%) combined with high yield tensile strength (1500 MPa) was obtained, which showed distinct advantages over all the other advanced high strength steels under development for a lightweight car body. Furthermore, the effect of austenite on enhancement of ductility in “Q&T” steels with a martensite matrix was elucidated, which suggested that the ductility was promoted by enhancing boundary sliding and delaying work hardening of the martensitic matrix.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?