Abstract:M-type barium ferrite powders doped with Zr4+ ions (BaFe12-xZrxO19 x = 0-0.4), possessing high permittivity and multi-resonant permeability, were synthesized by the sol-gel process. The single-phase hexagonal plate-like barium ferrites were formed with Zr4+ substituting Fe3+ at the 4f(1) sites initially and then at the 2b sites afterwards with increasing doping content. The H-a of the ferrites decreased from 15.75 kOe to 8.13 kOe with increasing Zr4+ from x = 0 to 0.4. The epsilon' and epsilon" of the ferrite with Zr4+ doping were increased to 7.7-6 and 3.4-1.5 over 18-40 GHz from 5.8-5 and 0.7-0.4 without doping, respectively. Contributed mainly by the enhanced permittivity, the matching thicknesses of the Zr4+ ions doped ferrites were as low as only similar to 1 mm or below, i.e. 1.5-3 times thinner than those reported recently. The complex permittivity was still close to the complex permeability in the doped ferrites. Hence, a strong reflection loss of similar to-50 dB could be attained and the absorptivity of electromagnetic (EM) power per unit thickness reached as high as 0.156% mu m(-1), i.e. 2-5 times higher than those of novel absorbing materials. The multi-resonance permeability peaks originated from Fe3+ ions, and exchange couplings among Fe3+, Fe2+ and O- contributed multiple reflection loss peaks and thus, a broad bandwidth of similar to 12 GHz (RL < -10 dB), which was 2-4 times broader than those normally reported. Consequently, the Zr4+-doped barium ferrites are promising for use as excellent absorbing materials in the millimeter wavelength frequency range.

Effect of BST Additive on the Complex Permeability and Permittivity of Z-type Hexaferrite in the Range of 1 MHz–1 GHz

Effects of BST Additive on Microstructure and Electromagnetic Parameters of Co2Z-type Hexagonal Ferrite

Effects of Perovskite Additives on the Electromagnetic Properties of Z-Type Hexaferrites

Sintering Behavior and Dielectric Property of BST-BZN Composite Ceramics

Effect of Sr/Ba Ratio on Dielectric Properties of BSTN Ceramics

Zr4+ Doping-Controlled Permittivity and Permeability of Bafe12-Xzrxo19 and the Extraordinary Em Absorption Power in the Millimeter Wavelength Frequency Range

The effects of Barium Strontium Titanate (BST) on the soft magnetic properties and loss performance of MnZn ferrites

The Effect of B2o3-Li2co3 Addition on Sintering Behavior and Dielectric Properties of Ba0.6sr0.4tio3 Ceramics

Effects of Zr4+ and Hf4+ substitution on the structure and dielectric response of Ba4Sm9.33Ti18O54 ceramics

Effect of sintering condition on microstructure and dielectric properties of BSTN composite ceramics

Enhanced low electric-field energy-storage performance in Ba0.9Sr0.1TiO3-Bi(Mg1/2Ti1/2)O-3 ceramics

High-frequency magnetic and dielectric properties of Ba1.5Sr1.5Co1Zn1Fe23O41 hexaferrites with Bi2O3 additives

Influence Of Mgtio3 On The Magnetic And Dielectric Properties Of Ba3co2fe24o41 Hexaferrite

Complex permittivity, permeability, and microwave absorption of Zn- and Ti-substituted barium ferrite by citrate sol–gel process

The influence of doped MgF2 on the dielectric properties of barium strontium titanate ceramics

Relaxor Behavior and Dielectric Properties of (1−x)ba0.6sr0.4tio3–xmg0.7zn0.3tio3 Composite Ceramics for Tunable Microwave Applications

Effects of different sintering temperature and Nb2O5 content on structural and magnetic properties of Z-type hexaferrites

The effect of Zn–B–Si–O addition on Ba0.7Sr0.3TiO3 by sol–gel process

The Effects of Bto with a Ptc Characteristic on the Mnzn Ferrites for Applications in the Frequency Range of 100-300Khz

B-site Modification of (ba0.6sr0.4)tio3 Ceramics with Enhanced Diffuse Phase Transition Behavior

Low-Temperature Sintering, Densification, and Properties of Z-type Hexaferrite with Bi<sub>2</sub>O<sub>3</sub>Additives