Abstract:In this paper, the effect of Si content on the microstructure and mechanical properties of the Al–1.2Mg– x Si–1.2Cu–0.6Mn cast alloy was investigated. The study aimed to explore the optimal addition of Si element to improve the comprehensive properties of alloys. The microstructure, phase composition and fracture morphology of the alloy were determined through OM, SEM, EBSD and XRD analysis. The Si content in the alloy ranged from 0.48 to 2.4 wt.%. With the increase of Si content, the number of strengthening phases increases, which improves the comprehensive properties of the alloy. When the Si content is 0.8 wt.%, the eutectic Mg 2 Si transforms from rod-shaped to larger block shaped, and the formation of coarse Mg 2 Si phase limits the elongation of the alloy. When the Si content is 2.4 wt.%, fine Al 2 Cu phases are present in this alloy and coexist with Al(Fe,Mn)Si phases, while an increase in the Si content appears as partially accompanied by an incipient crystalline Si phase around the Al(Fe,Mn)Si phase. The alloy exhibits a maximum tensile strength, yield strength and elongation of 198.2 MPa, 101.2 MPa and 4.96%, respectively, with a hardness of 80.94 Hv. It consists of five alloy phases, mainly α-Al, Mg 2 Si, Al(Fe, Mn)Si eutectic phase, Q-AlCuMgSi eutectic phase and the beginning crystalline silicon phase formed due to the increased Si content. The Si content can improve alloy strength, but there is some damage to the toughness of the alloy. Higher silicon alloy content results in the formation of fine Al 2 Cu eutectic. This result makes it possible to achieve a higher level of strength with a reduced loss of ductility in the alloy.

High Damping Properties of Mg–Si Binary Hypoeutectic Alloys

Microstructure and damping properties of Mg–Si binary hypoeutectic alloys

Effect of Mg on Nucleation Process of Recrystallization in Al–Mg–Si/SiCp Composite

Achieving high damping and excellent ductility of Al Mg alloy sheet by the coupling effect of Mg content and fine grain structure

Solid solution strengthening and damping capacity of Mg−Ga binary alloys

A Study on the Damping Capacities of Mg–Zn–Y-Based Alloys with Lamellar Long Period Stacking Ordered Phases by Preparation Process

The ultrahigh damping capacity of Mg-Sn-Y alloy

A Comparative Study on Microstructure, Mechanical Property and Damping Capacity of Hypoeutectic Al–Si–Cu Alloy for Different Casting Technologies

Calculation Based on the Formation of Mg2Si and Its Effect on the Microstructure and Properties of Al–Si Alloys

Temperature Damping Capacity and Microstructure Evolution of Mg–Al–Zn–Sn Alloy

Synergistic Effect of Sc and Excess Mg on the Microstructure and Mechanical Properties of Hypoeutectic Al-10Mg2Si Alloy

Simultaneous improvement of strength and damping capacity of Mg-Mn alloy by tailoring bimodal grain structure

Effect of alloying elements and heat treatment on damping capacity of Mg-Al alloys.

Strengthening Mechanism and Damping Properties of SiCf/Al-Mg Composites Prepared by Combining Colloidal Dispersion with a Squeeze Melt Infiltration Process

Effect of Mg addition on microstructure and mechanical properties of Al-Si-Cu-Fe alloy with squeeze casting

Microstructure control and performance evolution of hypereutectic Al–20Mg2Si alloy by novel Al–Ca–Sb master alloy

The Effect of Si Content on the Microstructure and Mechanical Properties of Al–1.2Mg–xSi–1.2Cu–0.6Mn Cast Alloy

Effect of Rare Earth Dy (dysprosium) on the Microstructures and Mechanical Properties of Hypereutectic Al–Si Alloy

Effects of Si Content and Ca Addition on Thermal Conductivity of As-Cast Mg⁻Si Alloys

Damping capacity of magnesium matrix composites fabricated by ultrasonic-assisted stir casting

Decreased dislocation density as an origin for the quench sensitivity of the Al-Si-Mg alloys with high Si content