Abstract:Synthesis of nanocomposites is challenging due to the difficulties in achieving homogeneous distribution of reinforcing particles in metal. In this paper, an in‐situ Al‐MgAl2O4 nanocomposite billet was prepared by the reaction of ɣ‐Al2O3 with molten Al and ultrasonication‐assisted impeller mixing. The microstructure of the composite showed homogeneously distributed MgAl2O4 crystals alongside their clusters in the Al matrix. Microstructural analysis revealed MgAl2O4 crystals distributed from 20 nm to 4 μm in size. The hardness was found to vary within the composite from 50 Hv for the matrix to 140 Hv for particle cluster regions. The grain size was reduced from 1000 μm in reference metal (CP Al) to 100 μm in the composite. The compression strength of the composite was increased substantially and higher strain hardening effect in comparison with Al was noticed in the compression test. The signatures of extensive plastic deformation such as dislocation pileups, deformed grains, grain boundary pinning etc. were observed in the composite via transmission electron microscopy. Damping properties of as‐cast composite were higher than those of CP Al in the temperature range from room temperature to 350 °C. After rolling the composite up to 40% reduction, the damping capacity (Tanδ) of the composite was found to increase marginally after 150 °C. Higher damping was found to reoccur after the annealing treatment of the composite. The improvement in damping capacity at RT was possibly influenced by the micron sized MgAl2O4 and at higher temperatures by the nano‐sized MgAl2O4 crystals. The reoccurrence of higher damping in the annealed composite underlined the stability of finer grains due to the grain boundary pinning by nano‐sized MgAl2O4 crystals. The studies on the damping property of the composite displayed the benefits of having dual size distribution of MgAl2O4 crystals (nm and μm) in the composite. This article is protected by copyright. All rights reserved.

Damping capacity of magnesium matrix composites fabricated by ultrasonic-assisted stir casting

Magnesium Matrix Nanocomposites Fabricated by Ultrasonic Assisted Casting

Ultra-High Damping Capacity of Oxide Reinforced Magnesium Matrix Composites by In Situ Synthesis

Microstructural evolution and property evaluation of in‐situ Al‐MgAl2O4 nanocomposite prepared by ɣ‐Al2O3 and ultrasonication‐assisted impeller mixing

A Study on the Damping Capacities of Mg–Zn–Y-Based Alloys with Lamellar Long Period Stacking Ordered Phases by Preparation Process

Damping performance of SiC nanoparticles reinforced magnesium matrix composites processed by cyclic extrusion and compression

Preparation and properties of nano-sized SiC particles reinforced AZ91D magnesium matrix composites

Strengthening Mechanism and Damping Properties of SiCf/Al-Mg Composites Prepared by Combining Colloidal Dispersion with a Squeeze Melt Infiltration Process

Graphene Nanoplatelets Reinforced Magnesium Matrix Composites Fabricated by Thixomolding

Effects of High Intensity Ultrasonic Processing on Preparation of SiC Nano-Particles Reinforced Magnesium Matrix Composite

Influence of ultrasonic processing on nano-sized particle dispersion in magnesium matrix nanocomposites

Damping behavior and energy absorption capability of porous magnesium

Damping characterization and its underlying mechanisms in CNTs/AZ91D composite processed by cyclic extrusion and compression

Mechanical and Wear Behaviour of Nano-Fly Ash Particle-Reinforced Mg Metal Matrix Composites Fabricated by Stir Casting Technique

Fabrication and Mechanical Properties of Mesoporous Silica Nanoparticles Reinforced Magnesium Matrix Composite

Foamability and mechanical properties of in situ submicron MgAl2O4p/Al composite foams by ultrasonic method

Effects of sonication amplitude on the microstructure and mechanical properties of AZ91E magnesium alloy

Magnesium-based nanocomposites synthesized using friction stir processing: an experimental study

Investigation on Mechanical and Fracture Behavior of Magnesium Composite Reinforced With Hybrid Fly Ash Particulates Synthesized via Friction Stir Processing Route

Influence of hybrid reinforcements on the mechanical properties and morphology of AZ91 magnesium alloy composites synthesized by ultrasonic-assisted stir casting

Experimental Analysis for the Performance Assessment and Characteristics of Enhanced Magnesium Composites Reinforced with Nano-Sized Silicon Carbide Developed Using Powder Metallurgy