Synthesis and Luminescence Properties of Red Long Afterglow Phosphor Y_2O_2S:Eu~(3+),Mg~(2+),Ti~(4+) by Sol-Gel Process

LIU Duo,HUANG Ping,LEI Xing,YANG Fan

2012-01-01

Abstract:The red long afterglow phosphor Y2O2S:Eu3+,Mg2+,Ti4+ material was synthesized by a sol-gel method using metal nitrate and tetrabulyl titanate as raw materials,acetyl acetone as a complexing agent.The performance of samples synthesised at different temperatures was investigated by X-ray diffraction,scanning electron microscopy and ?uorophotometer technique,respectively.The precursor of Y2O3:Eu3+,Mg2+,Ti4+ with a cubic crystal structure was obtained via the calcinations of the dry gel at 600 ℃ for 2 h.When the precursor was sulfurized at 1 050-1 150 ℃,the product was a mixture of Y2O3 and Y2O2S.The pure phase of Y2O2S:Eu3+,Mg2+,Ti4+ was obtained at 1 200 ℃ and the average particle size was approximately 150 nm,the phase of Y2O3 appeared again at 1 300 ℃.The main peaks of excitation spectra of the samples synthesized by sol-gel method showed blue-shift,compared to the sample obtained by solid-state reaction method,and the main peaks of emission spectrum at 616 and 626 nm were ascribed to 5D0 to 7F2 transition of Eu3+;The afterglow time of the sample was 40 min at the sulfurization temperature of 1 200 ℃.