Size dependence of ductile to brittle transition of Zr-based metallic glasses under multiaxial loading
Xiangkui Liu,Jian Kong,Xinxiang Song,Shuai Feng,Qipeng Wang,Yang Yang,Tianchi Wang
DOI: https://doi.org/10.1016/j.jmrt.2021.07.002
IF: 6.267
2021-09-01
Journal of Materials Research and Technology
Abstract:<p>The size dependence of ductile to brittle transition of Zr-based metallic glasses was systematically investigated by small punch test. It was found that the metallic glasses with thickness ranging from 50 to 700 μm displayed an obvious transition from ductility to brittleness. Compared with thick samples, thin samples exhibit higher strength and better plasticity, which is attributed to the size-dependent transformation from soft state to hard state dominated by the deformation factor (<span class="math"><math>α=τ/σ</math></span>). Specifically, two significant transitions in deformation behavior at sample thickness of 200 and 500 μm are attributed to two critical deformation factors of <span class="math"><math>αc1</math></span> and <span class="math"><math>αc2</math></span>, which are responsible for the initiation of circumferential and radial shear bands, respectively. Specifically, only several micro-cracks can be observed on sample surface with <span class="math"><math>α≤αc2</math></span>. While <span class="math"><math>αc1≥α≥αc2</math></span>, multiple radial shear bands are activated and uniformly distributed on the sample surface. Further, when <span class="math"><math>α≥αc1</math></span>, multiple circumferential shear bands primarily initiate under high shear stress and large number of radial and circumferential shear bands can be observed on sample surface. The initiation and interaction of multiple radial and circumferential shear bands significantly enhance the ductility of the samples with <span class="math"><math>α≥αc1</math></span>.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering