Abstract:Upon reducing the sample size into micrometer scale, an obvious brittle-to-ductile transition accompanied by a drastic change of failure mode from shattering to shear-banding was observed when compressing the brittle but strong Co55Ta10B35 bulk metallic glass (BMG). The shattering failure under macroscopic compression is dominated by splitting cracking, which completely differs from shear-banding and originates from extrinsic defects like inclusions. To reveal the critical conditions for shear-banding and splitting cracking, various micropillar specimens with intentionally introduced holes as extrinsic defects were tested, and the stress distributions at the failure moment were analyzed with finite element simulation. The shear plane criterion was found to be quite effective to estimate the nominal stress required for the failure dominated by shear-banding. However, brittle splitting cracking does not occur although the maximum tensile stress reaches the critical value, which is different from traditional brittle solids. To initiate splitting cracking, a high-tensile-stress region over a critical distance, which depends on defect size and fracture toughness of the BMG, is required. The critical conditions for shear failure and splitting cracking demonstrated in this approach can be used to estimate the failure conditions of various BMG components with complex geometries in a wide range of length scales, and to design tough composites based on brittle BMGs. As an example, a design criterion to avoid brittle splitting fracture of porous BMG materials is proposed.

Effects of sample sizes on compressive mechanical behaviors of Mg-based bulk metallic glasses

Coupling Effects of Thickness and Aspect Ratio on Deformation Behavior of Cu50Zr50 Metallic Glass

Size Effects on the Compressive Deformation Behaviour of A Brittle Fe-Based Bulk Metallic Glass

Effect of Pre-Existing Shear Bands on Mechanical Properties and Serration Behaviors in Bulk Metallic Glasses

Dual specimen-size dependences of plastic deformation behavior of a traditional Zr-based bulk metallic glass in compression

Casting effect on compressive brittleness of bulk metallic glass

Some Aspects of the Fracture Behaviour of Mg65cu25y10 Bulk Metallic Glass During Room-Temperature Bending

Specimen Size Effects on Zr-Based Bulk Metallic Glasses Investigated by Uniaxial Compression and Spherical Nanoindentation

Effect of medium-range ordered nanoclusters on compression deformation of Mg65Cu25Y10 metallic glasses

Effects of Aspect Ratio and Loading Rate on Room-Temperature Mechanical Properties of Cu-based Bulk Metallic Glasses

Formation of Mg–Cu–Zn–Y Bulk Metallic Glasses with Compressive Strength over Gigapascal

Compressive Fracture Characteristics of Ni42Cu5Ti19Zr22.5Al8Si3.5 Bulk Metallic Glass

Interpreting Size Effects of Bulk Metallic Glasses Based on A Size-Independent Critical Energy Density

Sample-Size Effects on the Compression Behavior of A Ni-Based Amorphous Alloy

Mg–Cu–Y–Ag Bulk Metallic Glasses with Enhanced Compressive Strength and Plasticity

Size Effects on the Fatigue Behavior of Bulk Metallic Glasses

Effect of Microstructures on the Compressive Deformation and Fracture Behaviors of Zr47Cu46Al7 Bulk Metallic Glass Composites

Uncovering the Inherent Size Dependence of Yield Strength and Failure Mechanism in Micron-Sized Metallic Glass

Strength, Plasticity and Brittleness of Bulk Metallic Glasses under Compression: Statistical and Geometric Effects

Size-dependent Failure of the Strongest Bulk Metallic Glass

Shear Stability of Metallic Glasses