Abstract:The conductive nano-Al/polyaniline composites were prepared by the milling method in the solid state. Here, aluminum nanostructures were prepared in two different mechanical methods, wire drawing and wire milling in the presence of lubricant oil. The effects of the preparation methods on the structures and morphologies of aluminum nanostructures were investigated by XRD and FESEM. The results show that the shape and size of aluminum nanoparticles in the preparation by the wire drawing method are significantly different than the wire milling method. The aluminum nanostructures were prepared by milling method have flake-like nanosheets while the wire drawing method leads to the formation of spherical ultrafine nanoparticles, which particles size are in the range of 30–60 nm. Then, polyaniline was produced using a solid-state polymerization process by the chemical reaction between aniline hydrochloride and potassium peroxydisulfate. Finally, nano-Al/polyaniline composites were prepared by mechanical milling at room temperature. The quantitative analysis was carried out with the materials analysis using diffraction (MAUD) method and weight fraction for aluminum and PANI were calculated 6.66% and 93.34%, respectively. Electrical conductivity measurements show the conductivity (1.2 × 10 −2 S cm −1 at 25 °C) for polyaniline emeraldine salt and (1.02 × 10 −3 S cm −1 at 25 °C) in nanocomposite respectively. The results show that by adding aluminum nanoparticles to the polymer the conductivity of nanocomposite (Al/PANI-ES) is lower than that for pure (PANI-ES). Thermogravimetry and differential thermal analysis curves show pure (PANI-ES) and nanocomposite (Al/PANI-ES) have a similar thermal degradation process. The total weight loss in TG curve of pure PANI-ES, in the temperature range 45–800 °C is 46.28% but, total weight loss observed in nanocomposite is 38.67%. Therefore, nanocomposite has higher thermal stability than that of the pure PANI-ES.

Preparation of conductive polyaniline/flake graphite composite and its electric conductivity mechanism

Novel polyaniline-LiNi0.5La0.02Fe1.98O4 nanocomposites prepared via an in situ polymerization

Preparation and Characterization of Polyaniline/Mmt Conductive Composites

Electric Conductivity and Thermorheology Properties of Polyacrylonitrile/Nylon6 Composites Filled with Carbon Black

Preparation And Electrical Properties Of Conducting Polyaniline-Polycarbonate Composite Films

Preparation and thermoelectric properties of polyaniline/NaFe4P12 composite

Experiments and Modeling of Thermal Conductivity of Flake Graphite/polymer Composites Affected by Adding Carbon-Based Nano-Fillers

Conducting Property of Unsaturated Polyester Composite

Hierarchical Polyaniline Core-Shell Nanocomposites Coated on Modified Graphite for Improved Electrical Conductivity Performance

A Novel Conductive Composites: Preparation And Electrical Property Of Polypyrrole Coated Carbon Nanotubes

Structure and electronic transport properties of polyaniline/NaFe4P12 composite

Modeling the In-Plane Thermal Conductivity of a Graphite/polymer Composite Sheet with a Very High Content of Natural Flake Graphite

Research on Electrical Properties of Carbon Filled Conductive Composites

Conductive nano-Al/polyaniline composites prepared via mechanical milling

Electrical and Structural Analysis of Conductive Polyaniline/polyacrylonitrile Composites

Preparation of Reduced Graphene Oxide/Polyaniline Composite Conductive Materials by Ultrasonic-Assisted In Situ Polymerization

Preparation and thermal conduction property of expanded graphite matrix composites

Electrically Conductive Polyaniline-Poly(vinyl Alcohol) Composite Films: Physical Properties and Morphological Structures

Preparation of a Graphene Nanosheet/polyaniline Composite with High Specific Capacitance

Preparing CNT/UHMWPE Composite and It’s Electrical Property Study

The effect of a conductive polyaniline/carbon black composite on the performance of a semiconductive layer