Abstract:Titania (TiO 2 ) nanofibers were fabricated by electrospinning three representative spin dopes made of titanium (IV) n -butoxide (TNBT) and polyvinylpyrrolidone (PVP) with the TNBT/PVP mass ratio being 1/2 in three solvent systems including N,N -dimethylformamide (DMF), isopropanol, and DMF/isopropanol (1/1 mass ratio) mixture, followed by pyrolysis at 500 °C. The detailed morphological and structural properties of both the as-electrospun precursor nanofibers and the resulting final TiO 2 nanofibers were characterized by SEM, TEM, and XRD. The results indicated that the precursor nanofibers and the final TiO 2 nanofibers made from the spin dopes containing DMF alone or DMF/isopropanol mixture as the solvent had the common cylindrical morphology with diameters ranging from tens to hundreds of nanometers, while those made from the spin dope containing isopropanol alone as the solvent had an abnormal concave morphology with sizes/widths ranging from sub-microns to microns. Despite the morphological discrepancies, all precursor nanofibers were structurally amorphous without distinguishable phase separation, while all final TiO 2 nanofibers consisted of anatase-phased TiO 2 single-crystalline grains with sizes of approximately 10 nm. The electrospun TiO 2 nanofiber mat is expected to significantly outperform other forms (such as powder and film) of TiO 2 for the solar cell (particularly dye-sensitized solar cell) and photo-catalysis applications.

Fabrication of ordered TiO2 nanoribbon arrays by electrospinning

Synthesis of aligned titanium-based oxide fibre arrays

Path-directed and maskless fabrication of ordered TiO2 nanoribbons.

Electrochemical Fabrication Of Highly Ordered Semiconductor And Metallic Nanowire Arrays

Fabrication of Aligned Fibrous Arrays by Magnetic Electrospinning

Helical nanoribbons fabricated by electrospinning

Fabrication and characterization of electrospun titania nanofibers

Electrospinning Of Fe, Co, And Ni Nanofibers: Synthesis, Assembly, And Magnetic Properties

Fabrication of Lithium Manganese Oxide Nanoribbons by Electrospinning: A General Strategy and Formation Mechanism

Hierarchical Structure Tio2 Micro/Nanofibers Prepared By Coaxial Electrospinning

Oriented Nanofibers by a Newly Modified Electrospinning Method

Fabricating Nanostructure Materials by Electrospinning Technique

Electrospinning of polymer nanofibers with ordered patterns and architectures.

Controllable Fabrication of TiO(2) 1D-Nano/micro Structures: Solid, Hollow, and Tube-in-tube Fibers by Electrospinning and the Photocatalytic Performance.

Ultralong Well-Aligned TiO2:Ln3+ (ln = Eu, Sm, or Er) Fibres Prepared by Modified Electrospinning and Their Temperature-Dependent Luminescence

Fabrication of TiO<sub>2</sub> Nanotube Arrays in Ethylene Glycol Electrolyte by the Electrochemical Anodization Method

Ribbon-like and spontaneously folded structures of tungsten oxide nanofibers fabricated via electrospinning

Electrospinning for Depositing Orderly Nanofiber Patterns

High Orientation Ordered Nanofibers Fabricated by Electrospinning

The Fabrication of Highly Ordered TiO2 Nanotube Arrays and Their Application in Dye-Sensitized Solar Cells

Nanofibers containing TiO2 nanoparticles formed using conventional and non-conventional electrospinning