Abstract:Hierarchical ZSM‐11 nanorods aggregates with external specific surface areas and mesoporous volumes were synthesized by hydrothermal crystallization with the addition of hexadecyltrimethylammonium bromide (CTAB). The catalytic performance of the catalyst for the reaction of cyclohexene hydration to cyclohexanol was tested. The nanorods aggregates showed a significant increase in the conversion of cyclohexene. A series of hierarchical ZSM‐11 nanorods aggregates were prepared by a hydrothermal crystallization method with the addition of cetyltrimethylammonium bromide (CTAB). The physical and chemical properties of the samples were characterized and the catalytic properties in the direct hydration of cyclohexene to cyclohexanol were also investigated. The characterization results showed that adding CTAB effectively increased the crystallinity of the zeolite, and the external specific surface areas and pore volume of the zeolite increased dramatically. With the increase of CTAB addition, more and more mesopores were formed which could be clearly seen from TEM micrograph. The ratio of Brønsted/Lewis acid decreased first and then increased with the increase of CTAB addition, with the lowest point appeared at the ratio of CTAB/SiO2 of 0.015. The zeolite synthesized at the CTAB/SiO2 ratio of 0.015 exhibited the highest reaction rate with the cyclohexene conversion as high as 14.23 %. The excellent performance of the hierarchical ZSM‐11 nanorods aggregates can be attributed to the lowest Brønsted/Lewis acid ratio and large mesoporous volume.

Synthesis of cyclohexene by solid super acid catalyst SO_4~(2-)/ZrO_2 and S_2O_8~(2-)/ZrO_2

Studies on Synthesis of Cyclohexanone Diethyl Acetal

Studing on Prepration of Cyclohexene by Various Catalysts

Synthesis of cyclohexanone glycerol ketal catalyzed by solid superacid catalyst SO2-4/ZrO2

Synthesis of Cyclohexene with Strong Acid Cation Exchange Resin as Catalyst

Catalytic synthesis of cyclohexanone ethylene ketal with solid superacid SO_4~(2-)/ZrO_2

Synthesis of Acetal With Solid Super Acid Catalyst S_2O_8~(2-)/ZrO_2

Research Progress in Cyclohexene Preparation by Cyclohexanol Catalytic Dehydration

Study of Catalytic Synthesis of Cyclohexanone Ethylene Ketal

Synthesis of acetal with solid super acid catalyst S2O8 2-/ZrO2

Synthesis of Di-2-ethylhexyl Adipate Catalyzed by Complex Solid Super Acid SO_4~(2-)/ZrO_2-TiO_2

Preparation of Fibrous SO42-/ZrO2-Nio Solid Acid Catalyst, Characterization and its Catalytic Properties

Novel WO3/SO42--ZrO2–TiO2 double bridge coordination catalyst hfor oxidation of cyclohexene

Synthesis of Benzocaine Catalyzed by Solid Superacid SO_4~(2-)/ZrO_2

Synthesis of cyclohexene catalyzed by iodine

The Synthesis of Di-2-ethylhexyl Maleate Catalyzed by Complex Solid Superacid SO2-4/ZrO2-TiO2

SYNTHESIS OF CYCLOHEXENE WITH STRONG ACID POLYSTYRENE CATION EXTHANGE RESIN AS CATALYST

Preparation and Catalyst Properties of S_2O_8~(2-)/Al-Zn-O Solid Acid Modified by Ce

Synthesis of Hierarchical ZSM‐11 Nanorods Aggregates and Catalytic Properties in Cyclohexene Hydration to Cyclohexanol

Optimization of Cyclohexanol Synthesis from Hydration of Cyclohexene

Catalytic Synthesis of Ethyl Chloroacetate with Nanosized Rare Earth Composite Solid Superacid SO_4~(2-)/ZrO_2-La_2O_3