Thermochemical and Thermionic Properties of Ionic Crystalline Films

H Kawano,Y Zhu,J Nakamura,S Sugimoto

DOI: https://doi.org/10.1016/s0040-6090(00)01224-4

IF: 2.1

2000-01-01

Thin Solid Films

Abstract:To clarify the thermochemical and thermionic properties of various layers of alkali halide (MX) such as LiF, LiI, NaBr, KCl, RbCl or CsCl, a thin film [θ̄0≃1−104 molecular layers (ML) at the start] of MX was prepared on a metal plate (∼0.04 cm2), and the absolute desorption rates (n+ and n0) of both positive ion (M+) and neutral molecule (MX0) were measured simultaneously in a vacuum as a function of sample temperature increased stepwise (by ∼5 K, approx. every 20 min) or constantly (∼0.3–80 K/s) by using our dual-ion source system. Theoretical analysis of the experimental data yields the following conclusions. (1) Below the melting point (Tm), more than 90% of MX are desorbed as MX0. (2) Its desorption energy (E0) increases up to the heat of sublimation as θ̄0 increases, suggesting that the film prepared at θ̄0⪡ 103 ML is partly amorphous rather than crystalline. (3) Ionic desorption, on the other hand, occurs mainly above Tm giving 1–3 peaks in a temperature-programmed desorption spectrum. (4) The desorption energy of M+ from MX is much larger than E0 and depends upon the species of X. (5) The film surface is very inhomogeneous in thermionic properties, and M+ is desorbed from those active sites having a high work function (e.g. 724 kJ/mol for LiCl). (6) The fractional surface area of the active sites over the film surface is as small as 10–2–10–5. (7) The ionization efficiency (∼n+/n0) is less than 10–2, usually increasing with a decrease in θ̄0.