Abstract:The as-cast and annealed Fe 76 Si 19.4 Nb 2.7 Cu 1.7 P 0.2 ribbons with width of 2.5 cm prepared by a single-roller cooling method were investigated. The structural properties of ribbons were studied by X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM). The XRD result shows the α-Fe crystal phase of annealed film. The average crystallite sizes of the as-cast and annealed ribbons are about 28 nm and 43 nm obtained from EF-SEM. The dielectric and magnetic properties of ribbons were tested over frequency ranges of 5 MHz to 300 MHz and 5 MHz to 3000 MHz using an Impedance Analyzer, respectively. The dielectric constant and dielectric loss of the as-cast ribbon decreases from 4.3 × 10 5 to 180 and from 3.01 to 0.06, while that of annealed ribbon decreases from 2.5 × 10 4 to 180 and from 3.01 to 1.31. The permeability decreased with increasing frequency at first of each ribbon and the value of annealed ribbon is bigger. It was observed that the permeability loss value of annealed ribbon is smaller at first and then bigger than that of as-cast ribbon. The smallest values of permeability of the as-cast and annealed ribbons are about 1.4 and 1.8. The minimum of the permeability loss of the as-cast ribbon is 0.008. The magnetic hysteresis loops were investigated using a vibrating sample magnetometer. The saturation magnetizations of the as-cast and annealed ribbons are 113 emu g −1 and 123 emu g −1 . The coercive fields of the as-cast and annealed ribbons are 259 A m −1 and 1130 A m −1 . The saturation magnetization and coercive field could become bigger due to the crystallize property.

Amorphous-crystalline Dual-Layer Structures Resulting from Metastable Liquid Phase Separation In(fe 50 Co 25 B 15 Si 10 ) 80 Cu 20 Melt-Spun Ribbons

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Structural and Magnetic Evolution of Rapidly Quenched Sm-Fe-Si-C Alloys

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Microstructure and magnetic properties of melt-spun Sm(Co0.58Fe0.31Cu0.04Zr0.05B0.02)z ribbons

Structures and Magnetic Properties of the Co7Hf Melt-Spun Ribbons

Study on structure and magnetic properties of Y<sub>2</sub>(Fe, Co)<sub>14</sub>B melt-spun ribbons

Study On Structure And Magnetic Properties Of Y-2(Fe, Co)(14)B Melt-Spun Ribbons

Magnetic hardening in amorphous alloy Sm60Fe30Al10

Structure and Properties of a Ribbon from FeCoNiSiB High-Entropy Alloy

The Crystallization Kinetics Study of Finemet-Co Amorphous Alloys

Structure and magnetic properties of spinodal decomposed Cu60Ni20Fe10Co10 ribbons with hard magnetism

Structure and Magnetic Properties of Melt-Spinning Pr(Fe0.6co0.4)(2) Alloys

Comprehensive study of the crystallization behavior, thermal stability, and magnetic properties of Co66.5Si15.5B12Fe4Ni2 amorphous ribbon

The Magnetic and Microstructural Evolution of Ni45mn24ga23co4cu4 Heusler Alloy Ribbons

Liquid and Solid Phase Separation During Melt Spinning and Annealing in Melt-Spun Cu–Cr Ribbons

Effect of melt-spinning speed on the microstructure and magnetic properties of Al–Cu–Fe alloy-doped SmCo5 ribbons

Interaction and Magnetic Properties of NdCeFeB Melt-Spun Ribbons

Comparative study on the structure and magnetic properties of Sm10Co60Fe15(Al, B)15 amorphous-nanocrystalline ribbons

Study of dielectric and magnetic properties with Fe76Si19.4Nb2.7Cu1.7P0.2 ribbons