Abstract:Following a long period of qualitative assessment of environmental cracking phenomenology, there has been recent emphasis on developing quantitative, mechanistically-based predictive models. This focus is driven by scientific and engineering concerns. For example, neither pressure vessel design nor evaluation codes incorporate the contribution of environmental cracking under static loading, nor do they differentiate between the large possible variations in both environment and material chemistry. Similarly, while numerous scientific hypotheses have been proposed to explain the crack advance process and related, contributing phenomena, ultimately their validity must withstand the scrutiny of quantification and comparison to measured cracking kinetics and observed component lifetimes. The benefits and approaches involved in predicting environmental cracking based on mechanistic modeling of crack advance and its underlying phenomena are discussed. The benefits and approaches involved in predicting environmental cracking based on mechanistic modeling of crack advance and the underlying phenomena are discussed. The formulation of a quantitative model from fundamental mechanisms has progressed most rapidly for the film rupture / slip dissolution mechanism of environmental crack advance. Specifically, for iron and nickel base alloys in high temperature water, identification, quantification and integration of the important underlying parameters has led to algorithms which predict crack growth rates over a wide continuum in static and dynamic stressing, metallurgical microstructure and solution chemistry applicable to light water reactors. For widely studied systems, e.g., stainless and low alloy steels in 288°C water, the predictions are within a factor of 2–3 for 90% of the data which span “initiation”, the possible roles of contributing, “secondary” crack advance processes in oxidation-based mechanisms, such as environmentally enhanced cleavage, spontaneous oxidation, etc. Similar efforts to identify and quantify the critical parameters and underlying processes in crack advance mechanisms involving hydrogen embrittlement, environmentally assisted cleavage, etc. are summarized. Conceptual approaches to and progress toward integrating these models with in-situ chemical and crack monitoring devices, with the goal of providing on-line evaluation, control and lifetime prediction of environmental cracking, are also discussed.

Fundamental modeling of environmental cracking for improved design and lifetime evaluation in BWRs

Developments in Quantification and Use of Environmental Cracking Mechanisms for Design and Lifetime Prediction

Life prediction by mechanistic modeling and system monitoring of environmental cracking of iron and nickel alloys in aqueous systems

Developing a Three-Dimensional Finite Element Analysis Approach to Simulate Corrosion-Induced Concrete Cracking in Reinforced Concrete Beams

Progress and opportunities in modelling environmentally assisted cracking

Towards Fully Automatic Modelling of the Fracture Process in Quasi-Brittle and Ductile Materials: a Unified Crack Growth Criterion

Modeling of Time to Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Corrosion-crack path based probabilistic model to predict the durability behavior of RC components

Corrosion Fatigue Mechanism of Nuclear-Grade Low Alloy Steel in High Temperature Pressurized Water and Its Environmental Fatigue Design Model

Development of Analogy Method for Thermal-Fatigue Crack Propagation in Pressurized Cylinder by Using Permeation Diffusion-Fracture Model

A Predictive Model for Corrosion Fatigue Crack Growth Rates in RPV Steels Exposed to PWR Environments

Environmentally Assisted Cracking of Forged 316LN Stainless Steel and Its Weld in High Temperature Water

Applications of phase field fracture in modelling hydrogen assisted failures

Approach of failure assessment of pressure vessels containing tilted cracks

CORROSION FATIGUE OF NUCLEAR-GRADE STAIN- LESS STEEL IN HIGH TEMPERATURE WATER AND ITS ENVIRONMENTAL FATIGUE DESIGN MODEL

On the role of intergranular nanocavities in long-term stress corrosion cracking of Alloy 690

Cracking assessment via a simplified approach – case of the gusset of the VeRCoRs nuclear power plant mock-up

Modeling of Time to Corrosion Cracking in Reinforced Concrete Structures

A REVIEW OF CORROSION FATIGUE OF STEELS FOR LWR PLANT IN HIGH TEMPERATURE AND HIGH PRESSURE WATER

Continuum damage mechanics method for fatigue growth of surface cracks

Modelling Stress-Diffusion Controlled Phase Transformations : Application to Stress Corrosion Cracking