Study on Pulse Electroplating of Ni-Cr-Mn Alloy Coatings
Zhi-tong ZHANG,Xin-yue WANG,Hai-peng LIU,Qing-bo MENG,Yun-gang LI,Hai-li YANG
DOI: https://doi.org/10.3969/j.issn.1000-4742.2018.01.001
2018-01-01
Abstract:Ni-Cr-Mn alloy coatings were prepared on the surface of Q235 steel by pulse electroplating.The bath composition and process conditions are as follows:NiSO4 · 6H2O 0.15 mol/L,CrCl3 · 6H2O 0.25 mol/L,MnSO4 · H2O 0.5 mol/L,sodium citrate 0.35 mol/L,NH4Br 15 g/L,NaCl 10 g/L,urea 10 g/L,H3BO3 15 g/L,sodium salt (SDS) 0.1 g/L,appropriate amount of additives,pH value 2.0～3.2,temperature 20～60 ℃,current density 5～17 A/dm2,duty cycle 20％,frequency 1 000 Hz,time 30 min.The Ni-Cr-Mn alloy coating obtained under the conditions of temperature 40 ℃,pH value 2.6 and current density 13 A/dm2 exhibited the best corrosion resistance.Compared to the Ni-Cr alloy coating,the corrosion resistance of Ni-Cr-Mn alloy coating was better,the self-corrosion potential was increased by 0.07 V and the self-corrosion current density was decreased by an order of magnitude.