Study on Microstructure and Corrosion Resistance of Alkaline Zn-Ni Alloy Plating

Xiao-dong LIU,Chao-yin NIE,Yang ZHAO,Yan-zhong NIE

DOI: https://doi.org/10.13718/j.cnki.xdzk.2015.06.028

2015-01-01

Abstract:A Zn‐Ni alloy coating was quickly prepared on 304 stainless steel surface in an alkaline Zn‐Ni al‐loy plating solution with the electrochemical deposition method .Its microstructure was testified with scan‐ning electron microscopy and X‐ray diffraction graph ,and the corrosion resistance of the Zn‐Ni alloy coat‐ing and the Zn coating was studied and compared with electrochemical workstation .The results showed that the crystal shape of the Zn‐Ni alloy coating obtained in this study was of the γ‐shape and that the con‐tent of nickel and zinc was 14.37% and 85.63% ,respectively .The corrosion resistance of the Zn‐Ni alloy coating was testified in environments with different dielectric solutions .The potential of the Zn‐Ni alloy coating was 245 mV higher than that of the Zn coating in a 5% NaCl solution ,which indicated the driving force on corrosion on the surface of the Zn‐Ni alloy was much less than that of Zn ,and the corrosion cur‐rent density was 0.15 times as much as that of Zn .The potential of the Zn‐Ni alloy coating was 59 mV higher than that of the Zn coating in a 1 mol/L NaOH solution ,and the corrosion current density was 0.86 times as much as that of Zn .The Zn‐Ni alloy film showed a strong corrosion resistance in either neutral or alkaline solution .