Abstract:Elemental powder blends with atomic composition of Cu 100− x Ta x ( x =10, 30, 50, 70, and 90) were ball milled in a SPEX mill at several temperatures (room temperature (RT), liquid nitrogen temperature (LN 2 T), −80 °C, and 95 °C) to examine the effect of milling temperature on the extent of alloying and microstructural refinement. For the Cu-rich powders (10< x <50), high-energy ball milling to steady state at all temperatures produced a mixture of nanocrystalline Cu and Ta with no observable extension of mutual solid solubility. Compared with milling at RT, cryomilling (LN 2 T) caused further refinement of Cu crystallites, while the same steady-state grain size was reached for Ta crystallites. On the Ta-rich side (50< x <90), ball milling at all temperatures led to refined Cu and Ta grain sizes. Partial amorphization seemed to be present, which apparently increased in extent with increasing contamination from the milling media upon extended milling. Very similar results were obtained for milling at RT and LN 2 T. It was concluded that high-energy ball milling at LN 2 T did not drastically enhance the amorphization reaction between Cu and Ta nor extend their mutual solubility. The limited power of cryomilling to alloy immiscible elements such as Cu-Ta is explained as a consequence of the inability to fully suppress, during energetic collisions, the atomic mobility responsible for phase separation even when the milling is conducted at the nominal LN 2 T. The temperature dependence of milling-induced microstructural refinement and alloying is analyzed in terms of the dynamics of the generation and annihilation of the nonequilibrium vacancies in an externally driven system. It is predicted that externally forced mixing as well as diffusion assisted by high-energy ball milling can be merely weakly temperature dependent between RT and LN 2 T. As a result, the extension of solubility by using cryomilling is feasible only in limited systems, and this process cannot be expected to alloy all immiscible elements.

Mechanical alloying of immiscible Pb-Al binary system by high energy ball milling

Study on the nano-crystalline and amorphous Al-Pb series powders synthesized by mechanical alloying

Synthesized by Ball Milling Al-Pb-Si-Sn-Cu Nanocrystalline Powder

Formation of nanocrystalline and amorphous phase of Al-Pb-Si-Sn-Cu powder during mechanical alloying

Mechanical Alloying of Immiscible Metallic Systems: Process, Microstructure, and Mechanism

Mechanical Alloying of Immiscible Elements: Ag-Fe Contrasted with Cu-Fe

Preparation of Nb3al by High-Energy Ball Milling and Superconductivity

Study on Phase Transformation and Thermodynamic and Kinetic of Al-Pb Powder During Mechanical Alloying

The Effect of Cu Addition and Milling Contaminations on the Microstructure Evolution of Ball Milled Al–Pb Alloy During Sintering

Amorphization in the AlC System by Mechanical Alloying

Variation of mechanical properties and microstructures of Al-Pb mixed powder during mechanical milling

Eff ects of Diff erent Mechanical Alloying Parameters on Microstructure of High Temperature Nanocrystalline Cu-Ta Alloys

A study of electromagnetic characteristics of Fe-Si-Al magnetic alloy

Effect of milling temperature on mechanical alloying in the immiscible Cu-Ta system

Fabrication Of Nanostructural Aluminum Alloy Powder With Ball Milling Method

Effect of mechanical milling on microstructure evolution and mechanical properties of Al–Zn–Mg–Cu–Si alloy fabricated via spark plasma sintering

Alloying of Al2Au intermetallic compound with Cu by the ball milling technique

Mechanical Alloying of the Immiscible Cu-60wt%Cr Alloy: Phase Transitions, Microstructure, and Thermodynamic Characteristics

Microstructure and Wear Properties of Al-Based Bearing Alloys Fabricated by Mechanical Alloying

Synchrotron X-ray Absorption Studies of Atomic-Level Alloying in Immiscible Mixtures

The research of processing of Zn/Al2O3 composite powders obtained by high energy ball milling of Al-ZnO