Abstract:Microstructural modifications of a thermally sprayed MCrAlY bond coat subjected to high-current pulsed electron beam (HCPEB) and their relationships with thermal cycling behavior of thermal barrier coatings (TBCs) were investigated. Microstructural observations revealed that the rough surface of air plasma spraying (APS) samples was significantly remelted and replaced by many interconnected bulged nodules after HCPEB irradiation. Meanwhile, the parallel columnar grains with growth direction perpendicular to the coating surface were observed inside these bulged nodules. Substantial Y-rich Al2O3 bubbles and varieties of nanocrystallines were distributed evenly on the top of the modified layer. A physical model was proposed to describe the evaporation-condensation mechanism taking place at the irradiated surface for generating such surface morphologies. The results of thermal cycling test showed that HCPEB-TBCs presented higher thermal cycling resistance, the spalling area of which after 200 cycles accounted for only 1% of its total area, while it was about 34% for APS-TBCs. The resulting failure mode, i.e., in particular, a mixed delamination crack path, was shown and discussed. The irradiated effects including compact remelted surface, abundant nanoparticles, refined columnar grains, Y-rich alumina bubbles, and deformation structures contributed to the formation of a stable, continuous, slow-growing, and uniform thermally grown oxide with strong adherent ability. It appeared to be responsible for releasing stress and changing the cracking paths, and ultimately greatly improving the thermal cycling behavior of HCPEB-TBCs.

A study on gradient thermal barrier coatings by EB-PVD in a cyclic high-temperature hot-corrosion environment

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Influence factors of high temperature oxidation for Pt-modified-aluminide bond coatings

Characterisation and Oxidation Behaviour of Plasma Surface Alloyed on Γ-Tial Alloy

Thermal shock behaviors and failure mechanisms of EB-PVD thermal barrier coatings using radiant heating

Failure Behaviors of EB-PVD Thermal Barrier Coatings under Isothermal Oxidation and Thermal Cycling Conditions

Study on Performance of 8YSZ Thick Gradient TBC

Preparing and Study of EB-PVD Thermal Barrier Coatings on Titanium Substrates

Isothermal and Cyclic Oxidation Performance of Vertically Cracked and Columnar Thermal Barrier Coating Structures Produced Using Axial Suspension Plasma Spraying Process

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Enhancing the performances of EB-PVD TBCs via overlayer Al-modification

Thermal cycling of EB-PVD TBCs based on YSZ ceramic coat and diffusion aluminide bond coat

Study of Failure of EB-PVD Thermal Barrier Coating Upon Near-Α Titanium Alloy

Comparative Study on Microstructure Evolution and Failure Mechanisms of Ordinary and Refurbished EB-PVD TBC under Cyclic Oxidation

Thermal Cycling Behavior of Thermal Barrier Coatings with MCrAlY Bond Coat Irradiated by High-Current Pulsed Electron Beam

Bonding and Thermal-Mechanical Property of Gradient NiCoCrAlY/YSZ Thermal Barrier Coatings with Millimeter Level Thickness

Effects of a nano carbide coating fabricated by EB-PVD on the interfacial stability of aluminide coated superalloy

Study of stress-driven cracking behavior and competitive crack growth in functionally graded thermal barrier coatings

Microstructure and Thermal Cycling Behavior of Thermal Barrier Coating on Near-Α Titanium Alloy

Structural Design and High Temperature Oxidation Behavior of MCrAlY Bond Coating in the Thermal Barrier Coating System

Failure Behavior Study of EB-PVD TBCs under Salt Spray Corrosion and Thermal Shock Cycles