Abstract:In this work, two kinds of YSZ nano powders were used as the raw materials to prepare thermal barrier coatings (TBC) via atmospheric plasma spraying. Firstly, raw materials with different original morphologies constitute feedstocks with varying internal structures. Secondly, these feedstocks, after spraying, form TBCs with different structures and porosity. Based on this, the differences in the morphologies of the raw materials may result in variations in the performance of the coatings. Therefore, the high-temperature performance of the corresponding TBCs was assessed comprehensively. Notably, the TBC prepared from flaky-YSZ (FYSZ) nano raw materials exhibited failure after only 84 thermal shock cycles, while the TBC prepared from granular-YSZ (GYSZ) nano raw materials maintained functionality even after 100 thermal shock cycles. Meanwhile, the GYSZ TBC demonstrates a better resistance to high-temperature oxidation with slower TGO growth. The failure mechanism of the TBCs was analyzed, focusing on the morphologies and structural characteristics. The findings highlight that disparities in raw materials' morphologies play a pivotal role in regulating the high-temperature service performance of the TBCs. The GYSZ raw materials are conducive to the formation of denser feedstocks, leading to decreased porosity in the coatings. In addition, their small size and uniform particle distribution facilitate the formation of columnar grains in the coating, enhancing the interlayer bonding strength of the GYSZ TBC. Consequently, during high-temperature service, the GYSZ TBC can effectively impede the growth of the thermally grown oxide (TGO) and alleviate the associated thermal mismatch stress, thereby ensuring a prolonged service life of the TBC. This work establishes a theoretical foundation for designing the performance of TBCs based on modulating the morphologies of raw materials.

Study on Performance of 8YSZ Thick Gradient TBC

Bonding and Thermal-Mechanical Property of Gradient NiCoCrAlY/YSZ Thermal Barrier Coatings with Millimeter Level Thickness

Gradient Thermal Cycling Behavior of a Thermal Barrier Coating System Constituted by NiCoCrAlY Bond Coat and Pure Metastable Tetragonal Nano-4Ysz Top Coat

Microstructural Design and Thermal Cycling Performance of a Novel Layer-Gradient Nanostructured Sc2O3–Y2O3 Co-Stabilized ZrO2 Thermal Barrier Coating

Thermal Cycling Behavior of Nanostructured and Conventional Yttria-Stabilized Zirconia Thermal Barrier Coatings Via Air Plasma Spray

Microstructure and Thermal Cycling Behavior of Thermal Barrier Coating on Near-Α Titanium Alloy

The Influence of Temperature Gradient Across YSZ on Thermal Cyclic Lifetime of Plasma-Sprayed Thermal Barrier Coatings

Thermal cycling of EB-PVD TBCs based on YSZ ceramic coat and diffusion aluminide bond coat

Gradient thermal cyclic behaviour of La2Zr2O7/YSZ DCL-TBCs with equivalent thermal insulation performance

Study on gradient structure and interface mechanical properties of n–8YSZ/AlCoCrFeNi high–entropy coatings

Cracking Behavior of Gd2Zr2O7/YSZ Multi-Layered Thermal Barrier Coatings Deposited by Suspension Plasma Spray

Study on the Microstructure Evolution of Nano and Micron-size Thermal Barrier Coatings during Thermal Cycling

Performance of TBCs system due to the different thicknesses of top ceramic layer

Thermal shock behavior of 8YSZ and double-ceramic-layer La 2Zr 2O 7/8YSZ thermal barrier coatings fabricated by atmospheric plasma spraying

A comparative study on the performance of suspension plasma sprayed thermal barrier coatings with different bond coat systems

Investigation of Thermal Shock Behavior of Multilayer Thermal Barrier Coatings with Superior Erosion Resistance Prepared by Atmospheric Plasma Spraying

Thermal Failure of Nanostructured Thermal Barrier Coatings with Cold-Sprayed Nanostructured NiCrAlY Bond Coat

Thickness-related failure behaviors of the thermal barrier coatings under thermal gradient cycling

Preparation and High-Temperature Performance of Sc2O3-Y2O3 Co-Stabilized ZrO2 Thermal Barrier Coatings

The Effect of Two Raw YSZ Materials with Different Morphology on TBCs Via Atmospheric Plasma Spraying: Microstructures and High-Temperature Performance

Thermal shock performance and failure behavior of Zr6Ta2O17-8YSZ double-ceramic-layer thermal barrier coatings prepared by atmospheric plasma spraying