Abstract:Bifunctional initiators with two labile groups ( e g peroxides or azo groups) are frequently used in the polymer industry for the synthesis of vinyl polymers and resin curing In general, there are two types of bifunctional initiators: one is symmetrical bifunctional initiators containing two labile groups of equal structure, the other is unsymmetrical bifunctional initiators containing two labile groups of unequal structure One of the potential advantages of using bifunctional initiators is that high polymer molecular mass and high polymerization rate can be obtained simultaneously by controlling the initiator decomposition rate through optimal reaction temperature programming For free radical polymerization of methyl methacrylate (MMA) with monofunctional initiators, the kinetics is reasonably well understood in both low and high monomer conversion regimes However, the presence of an additional labile group in bifunctional initiators makes the polymerization kinetics very complicated. This is because labile groups such as peroxides become redistributed repeatedly in the growing and inactive polymers and they are engaged in further initiation, propagation, chain transfer and termination reactions during the course of polymerization. The effects of temperature and initiator concentration on the kinetics of MMA bulk polymerization initiated by 2,5 dimethyl 2,5 bis(2 ethyl hexanoyl peroxide) hexane (TX 141) were investigated.The energy of activation of MMA bulk polymerization initiated by TX 141 was about 91 kJ·mol -1 , and that of TX 141 decomposition was about 140 kJ·mol -1 , which was more close to the experimental data.The reaction order of TX 141 concentration was about 0 72,because there was mono and bi molecule termination. The kinetic comparison initiated by TX 141 and benzoyl peroxide (BPO) with the same half life period showed that the kinetics was the same when the concentration of TX 141 was half of that of BPO.But, the number average molecular mass ratio of that initiated by TX 141 to that by BPO was from 1 2 to 1 33 increasing with the conversion.There was an exothermal peak in the DSC curve of polymer initiated by TX 141 at low conversion, but there was no peak at high conversion and no peak was observed for the polymer initiated by BPO.It was shown that the two functional groups of bifunctional initiator decomposed at different times during the polymerization process.

Free-radical Crosslinking Copolymerization of Methyl Methacrylate/Triallyl Isocyanurate

INFLUENCE OF MONOMER COMPOSITION ON THE CHAIN TRANSFER COEFFICIENT IN METHYL METHACRYLATE/BUTYL ACRYLATE RAFT COPOLYMERIZATION

Influence of Small Amount of Co-Monomers on Acrylonitrile Polymerization in Dimethylformamide (DMF) Solution

Kinetics of methyl methacrylate and n-butyl acrylate copolymerization mediated by 2-cyanoprop-2-yl dithiobenzoate as a RAFT agent

Emulsion Copolymerization of Butyl Acrylate with Cationic Monomer Using Interfacial Redox Initiator System

Study of Kinetic of Emulsion Copolymerization of Methyl Methacrylate/ethyl Acrylate

Effects of Monomer Polarity on Mma/Ba/Nama Emulsifier-Free Emulsion Copolymerization

Kinetics of methyl methacrylate polymerization initiated by bifunctional initiator

Microwave-Assisted Synthesis of Cross-Linked Co-poly(itaconic anhydride-methyl methacrylate): The Effects of the Molar Ratio and Cross-Linking Agent on the Thermal Stability

In-Situ Heterogenous Polymerization of Methyl Methacrylateonto Nanometer Calcium Carbonate Particles

Fundamental Study on Preparation Process and Structure Coutrol of PBA/PMMA

STATISTICS- KINETIC MODEL SIMULATION AND EXPERIMENTAL RESEARCH OF MMA/EGDMA RADICAL CROSSLINKING PSEUDO - TRI - POLYMERIZATION

Atom Transfer Radical Polymerization of Methyl Methacrylate Induced by an Initiator Derived from an Ionic Liquid

The effect of monomer polarity on MMA/BA/ Sodium methacrylate emulsifier-free emulsion copolymerization

Improvement of the physical properties of poly(methyl methacrylate) by copolymerization with N -pentafluorophenyl maleimide; zero-orientational and photoelastic birefringence polymers with high glass transition temperatures

Copolymers of methyl methacrylate with N‐trifluorophenyl maleimides: High glass transition temperature and low birefringence polymers

The Use Of Epsilon-Caprolactone As A Polymerizable Solvent For The Atom Transfer Radical Polymerization Of Mma At Low Temperature

Synthesis of Poly(IB‐co‐VBDC)‐g‐PMMA Via Photo‐initiated Free Radical Graft Polymerization

Synthesis and Cross-linking Properties of MMA/BA/DAAM Copolymer Emulsion

Isotactic Copolymerization of Methyl Methacrylate (MMA) with Alkyl Acrylates

The Molecular Structure Control of Butyl Methacrylate/acrylamide (Co)polymers