Abstract:Titania-based nanocomposites have recently attracted much attention due to their unique structure and properties. Titania has been known to have three crystal phases: brookite, anatase and rutile. The anatase titania has the highest photoactivity than the other two phases. Meanwhile Ohtani et al. [1] reported that amorphous titania has a negligible photoactivity compared to the crystalline titania. Much work has been conducted on the optimization of catalytic properties of titania used in the photodegradation of organic pollutants in water by either using modified titania or thin titania films. Many researches indicated that dopants, such as many oxides, can effectively suppress the transformation of anatase into rutile by improving the onset transformation temperature [2]. Silica-titania mixed oxide is considered a potential candidate because it is used as not only a good photocatalyst itself but also a support material for other chemical reaction catalysts [3, 4]. 30SiO2/TiO2 powders (30 denotes the weight percent of silica) were prepared by sol-gel process. Ti(OBu n )4 and TEOS were used as precursors of titania and silica respectively. After TEOS was stirred in a mixture solution of pure ethanol, distilled water and hydrochloric acid for 1 h, Ti(OBu n )4 was added slowly into the mixture. The sol of SiO2/TiO2 was obtained after another two hours’ vigorous stirring and cooled to room temperature. The gel was calcined at different temperatures and then ground into fine powders. The distilled water solution of methyl orange (with a concentration of 25 mg/L) was chosen for photodegradation. 0.2 g powders were added into 40 ml of the above solution with vigorous agitation under the mercury light. A 756MC UV-VIS spectrometer was used to record the change of concentration of the methyl orange. FT-IR spectra was obtained by a Bruker EQUINOX55 spectrometer. TEM and HREM observations were carried out using a Jeol-2010 electron microscope. The XRD patterns were made in a D/max3A diffractometer with Cu Kα radiation. The crystallite size of powders was determined by Scherrer equation. Electron spin resonance measurements were made with a Bruker paramagnetic spectrometer. X-ray photoelectron spectroscopy (XPS) spectra of the sample were obtained with an NP-1 using the Mg Kα excitation source and the binding energies referenced to the C1s hydrocarbon line at 284.6 eV. The atomic ratios were obtained by intergrating the areas under the peak. Photodegradation for methyl orange with 30SiO2/ TiO2 samples calcinated at different temperature under UV irradiation is illustrated in Fig. 1. The results of other samples heated at temperatures higher than 850 ◦ C were not shown in this figure because further increase of the calcination temperature decreased the decomposition rate. It can be seen that decomposition rate of the samples fired at 400 ◦ C and 500 ◦ Ci s low. When the calcination temperature was further increased to 600 ◦ C, the higher photoactivity than Degussa P25’s was obtained. The sample heated at 800 ◦ C has the best photoactivity about 2 times higher than the Degussa P25.

Photocatalytic Activity of Titania Prepared by Sol-Gel Method for Air Cleaning

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Preparation of TiO2/SiO2 Aerogels by Non-supercritical Drying Method and Their Photocatalytic Activity for Degradation of Pyridine

Preparation and Photocatalytic Activities of Nanocrystal Titania

PHOTODEGRADATION OF FORMALDEHYDE OF DOPED TITANIA NANOCRYSTALS PREPARED BY SOL-GEL SYNTHESIS AND HYDROTHERMAL PROCESSING

Enhanced photoactivity of silica-titania binary oxides prepared by sol-gel method

Photocatalytic activity of epoxide sol–gel derived titania transformed into nanocrystalline aerogel powders by supercritical drying

Preparation of Porous Nano-titania and Its Photocatalytic Property for the Degradation of Rhodamine B

Sol-Gel Preparation and Visible Light Photocatalytic Activity of Nitrogen Doped Titania

Nanocrystalline anatase TiO2 photocatalysts prepared via a facile low temperature nonhydrolytic sol–gel reaction of TiCl4 and benzyl alcohol

Photocatalytic Degradation of Acetaldehyde on Mesoporous Tio2: Effects of Surface Area and Crystallinity on the Photocatalytic Activity

Photocatalytic Activity of Pure Rutile Particles Derived from A Photo-Assisted Sol-Gel Method

Preparation of Porous Titania Thin Film and Its Photocatalytic Activity

Preparation of TiO_2 Nanoparticle and Their Photocatalytic Property

TiO2 for efficient photocatalytic decomposition of acetaldehyde: An investigation of the effects of annealing temperature, humidity, and binder

Photocatalytic activity of TiO2 prepared by different solvents through a solvothermal approach

Preparation and Photocatalytic Activity of TiO2 with Different Crystal Structures

Low Temperature Synthesis of Crystalline Mesoporous Titania with High Photocatalytic Activity by Post-Treatment in Nitric Acid Ethanol Solution

Synthesis And Characterization Of Titania Prepared By Using A Photoassisted Sol-Gel Method