Abstract:Magnetocaloric cooling offers the potential to improve the efficiency of refrigeration devices and hence cut the significant CO2 emissions associated with cooling processes. A critical issue in deployment of this technology is the mechanical degradation of the magnetocaloric material during processing and operation, leading to limited service-life. The mechanical properties of hydrogenated La(Fe,Mn,Si)13-based magnetocaloric material are studied using macroscale bending tests of polycrystalline specimens and in situ micropillar compression tests of single crystal specimens. The impact of hydrogenation on the mechanical properties are quantified. Understanding of the deformation/failure mechanisms is aided by characterization with transmission electron microscopy and atom probe tomography to reveal the arrangement of hydrogen atoms in the crystal lattice. Results indicate that the intrinsic strength of this material is ~3-6 GPa and is dependent on the crystal orientation. Single crystals under compressive load exhibit shearing along specific crystallographic planes. Hydrogen deteriorates the strength of La(Fe,Mn,Si)13 through promotion of transgranular fracture. The weakening effect of hydrogen on single crystals is anisotropic; it is significant upon shearing parallel to the {111} crystallographic planes but is negligible when the shear plane is {001}-oriented. APT analysis suggests that this is associated with the close arrangement of hydrogen atoms on {222} planes.

Hydrogenation-induced variation in crystal structure and heat capacity of magnetic regenerative material Er3Ni

Hydrogenation Induced Change in Structures, Magnetic Properties and Specific Heats of Magnetic Regenerative Material Erni and Erni2

Analysis of hydrogenation of regenerative material Er3Ni and its reaction product

Hydrogen absorption characteristics and structural transformation during the hydrogenation process of Er3Ni

Hydrogen induced structural and magnetic transformations in magnetic regenerator materials ErNin (n=1, 2) and HoCu2

Hydrogenation Reaction Characteristics and Properties of Its Hydrides for Magnetic Regenerative Material HoCu 2

Large Field-Induced Magnetocaloric Effect in Ni$_{43}$Mn$_{46 - {\rm X}}$v$_{\rm X}$sn$_{11}$ Heusler Alloys

Study on Reaction Characteristics of Er3ni Hydrogenation

Refrigeration performance enhancement of pulse tube refrigerators with He–H2 mixtures and Er3NiHx regenerative material

The effect of temperature on the electrode properties of the directly prepared Ti3Ni2 alloy

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Large Magnetocaloric Effect of PrNi Compound at Liquid-Hydrogen Temperatures

The effect of hydrogen on the multiscale mechanical behaviour of a La(Fe,Mn,Si)13-based magnetocaloric material

Excellent Mechanical Properties and Specific Heat Capacity of Er3+xNi Binary Alloys

Effect of Hydrogenation on the Magnetic and Magnetocaloric Properties of Rare Earth Intermetallic Compounds Tb0.33Ho0.33Er0.33Ni and Dy0.33Ho0.33Er0.33Ni

Effects of Magnetic Annealing Temperature on Rate Properties of Nd0.75Mg0.25(Ni0.8Co0.2)3.8 Hydrogen Storage Alloys

Relative Cooling Power Enhancement of the Magnetic Refrigeration in Ni$_2$MnIn based Hesuler Alloys

Hydrogen Absorption of Nddyfeconbcub Sintered Magnets

Effect of heat treatment on the microstructure and properties of Ni based soft magnetic alloy

Crystal structures and hydrogenation–dehydrogenation characteristics of Er(Ni 1− x Mn x ) 2

Magnetic Properties and Magnetocaloric Effects in R3Ni2 (R = Ho and Er) Compounds