Abstract:In order to improve the activation behavior of Ti1.02Cr1.1Mn0.3Fe0.6 alloy with high hydrogen desorption pressure for hybrid hydrogen storage vessel application, the rare earth (RE) doped Ti1.02Cr1.1Mn0.3Fe0.6RE0.03 (RE = La, Ce, Ho) alloys were prepared by induction levitation melting. The effect of rare earth doping on the microstructures and hydrogen storage properties was also investigated systematically. The results show that Ti1.02Cr1.1Mn0.3Fe0.6 alloy displays a single C14 Laves phase, and there is a secondary phase of rare earth oxide in the RE doped alloys. The RE doping strategy can expand the unit cell volume of C14 Laves main phase. After RE doping, the activation behavior of the Ti1.02Cr1.1Mn0.3Fe0.6RE0.03 alloy is obviously improved and the hydrogen storage capacity is increased, while the hydrogen desorption plateau pressure is decreased. Moreover, the RE-free alloy can hardly absorb hydrogen at room temperature under 34-43 MPa hydrogen pressure, but all RE-doped alloys can absorb hydrogen to saturation under the same condition. The decline of pressure plateau is inversely proportional to the atomic number of RE. Among the studied alloys, the Ti(1.02)Cr(1.1)Mn(0.3)Fe(0.6)La0.03 alloy shows the best overall properties and can be fully activated at room temperature. Its hydrogen absorption pressure is 39.31 MPa and 51.27 MPa under 298 K and 318 K, respectively. Its hydrogen storage capacity is up to 1.715 wt% and the dissociation enthalpy is 16.63 kJ/mol H-2 with a desorption plateau slope of 0.098. (C) 2017 Published by Elsevier B.V.

Hydrogen induced structural and magnetic transformations in magnetic regenerator materials ErNin (n=1, 2) and HoCu2

Hydrogenation-induced variation in crystal structure and heat capacity of magnetic regenerative material Er3Ni

Hydrogenation Induced Change in Structures, Magnetic Properties and Specific Heats of Magnetic Regenerative Material Erni and Erni2

Hydrogenation Reaction Characteristics and Properties of Its Hydrides for Magnetic Regenerative Material HoCu 2

Crystallographic And Magnetic Properties Of The Hydrides R3fe29-Xcrxhy (R = Y, Ce, Nd, Sm, Gd, Tb, And Dy)

Effect of Rare Earth Doping on the Hydrogen Storage Performance of Ti1.02Cr1.1Mn0.3Fe0.6 Alloy for Hybrid Hydrogen Storage Application

Influence of Hydrogen on the Magnetic Properties of Fe85Zr3.5Nb3.5B7Cu1 Nanocrystalline Alloy

Hydrogen absorption characteristics and structural transformation during the hydrogenation process of Er3Ni

Hydrogenation and Anisotropic Expansions in R3fe29-Xtx (R = Y, Ce, Nd, Sm, Gd, Tb and Dy; T = V and Cr)

Effect of Hydrogenation on the Magnetic and Magnetocaloric Properties of Rare Earth Intermetallic Compounds Tb0.33Ho0.33Er0.33Ni and Dy0.33Ho0.33Er0.33Ni

Cristallographie and magnetic properties of hydride R3Fe29.xTxHy (R=Y, Ce, Nd, Sm, Gd, Tb and Dy; T=V and Cr)

A Study on the Effect of Hydrogen in the Compounds with Thmn12-Type Structure

A Study on the Effect of Hydrogen in the Compounds with BaCd11-type Structure

Improved magnetic properties and fracture strength of NdFeB by dehydrogenation

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Crystallographic and Magnetic Properties of R3Fe29-xTx and Their Nitrides, Carbides and Hydrides

Role of hydrogen in Nd–Fe–B sintered magnets with DyH x addition

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Investigation of Significant Magnetic Transformation for Hydrogenated ZnFe2O4 Nanoparticles

Ferromagetic-paramagnetic transformation in hydrogenated ferrous titanate

The effect of hydrogen on the multiscale mechanical behaviour of a La(Fe,Mn,Si)13-based magnetocaloric material