(Ba0.5Sr0.5)TiO3 modification on etched aluminum foil for electrolytic capacitor

Yin Hua Wang,Jun Yang,Jian Zhong Wang
DOI: https://doi.org/10.1016/j.ceramint.2007.03.004
IF: 5.532
2008-01-01
Ceramics International
Abstract:A new method was proposed to form (Ba0.5Sr0.5)TiO3–Al2O3 composite oxide film on etched aluminum foils. The specimens were covered with (Ba0.5Sr0.5)TiO3 (BST) layer by dip-coating in citrate solution and subsequent heat-treatment under 400–650°C, finally by anodizing in a hot boracic acid and borate solution. The BST powders heated under different temperatures were characterized by X-ray diffraction (XRD) and the specific capacitance of the coated specimens heat-treated under different temperatures and times was measured. It is found that the specific capacitance increases initially with enhancing the temperature and reaches to maximum at 550°C, but slightly decreases with the heat-treatment time. The capacitance was increased by about 35% after BST coating.