UV etched random copolymer membrane coated PBO fibers/cyanate ester wave-transparent laminated composites
Lin Tang,Junliang Zhang,Chunliang Wu,Yusheng Tang,Hao Ma,Jie Kong,Junwei Gu
DOI: https://doi.org/10.1016/j.compositesb.2021.108680
2021-05-01
Abstract:<p>Poly (<em>p</em>-phenylene-2,6-benzobisoxazole) fibers treated by random copolymer P(S<em>-co</em>-BCB-<em>co</em>-MMA) membrane and UV etching ( fibers) are performed as reinforcement, bisphenol AF/amantadine modified bisphenol A cyanate ester (AEAF-<em>co-</em>BADCy) resin as polymeric matrix, and the fibers/AEAF-<em>co</em>-BADCy wave-transparent laminated composites were then fabricated. When the P(S-<em>co</em>-BCB-<em>co-</em>MMA) membrane thickness is 62.3 nm and the UV etching time is 96 h, fibers display the best interfacial compatibility with AEAF-<em>co-</em>BADCy resin, and the corresponding wave-transparent laminated composites present the optimal comprehensive performance. Interlaminar shear strength (ILSS) and flexural strength are 50.2 and 745.6 MPa, 27.4% and 21.6% higher than those (ILSS of 39.4 MPa, flexural strength of 613.3 MPa) of pristine PBO fibers/AEAF-co-BADCy wave-transparent laminated composites, respectively. And the composites possess low complex permittivity and tan<em>δ</em>, corresponding |<em>T</em>|<sup>2</sup> in the X band is 88.9–94.2%. High-frequency structural simulation (HFSS) results demonstrate that the radome from the composites displays high <em>|T|</em><sup>2</sup> of 89.1–93.1% in the X-band, close to the theoretical calculation value. This work provides a certain theoretical guidance for fabricating lightweight, high strength, and high |<em>T</em>|<sup>2</sup> polymer matrix wave-transparent composites, and further broadens the application of PBO fibers and cyanate ester resins in aviation/aerospace, 5G communication services, electronic information, and other fields.</p>
engineering, multidisciplinary,materials science, composites