Abstract:Herein, Si3N4 powders of comparatively high α‐phase but with distinct morphologies, especially α‐Si3N4 fibers, were successfully prepared by a developed combustion synthesis (CS) strategy. Different proportions of Fe and Fe2O3 were innovatively doped in reactants as additives to control the phase constitution and their relative percentage, as well as morphologies of final microstructures. One step further, the effects of Fe‐contained impurities on the CS process were rationally proposed and verified based on a series of meticulous designed experiments. It turns out that two contradictory effects of metal Fe on the formation of α‐Si3N4 synergistically play vital roles in the CS reaction. The existence of metal Fe can accelerate the crystallization of the amorphous SiO2, which act as protection layer outside the Si powders and subsequently promote the generation of gaseous SiO. These gaseous SiO easily reacts with N2 and eventually form α‐Si3N4. On the other hand, the formation of β‐Si3N4 will be promoted by the assistance of some liquid phases, and in this case, they mainly come from the reaction between Fe and Si. For this study, when the content of doped Fe is below 2 mol%, the prior effect on promoting α‐phase content is pronounced. Otherwise, the latter dominates the CS process as the content of Fe additive is further increased above 2 mol%. In a different way, Fe2O3 mainly encourages the formation of β phase through the large amount of newly generated liquid phases, although the reduced SiO2 and Fe may still promote the α/β ratio on some extent.

Tailoring of phase assemblage and grain morphology of (Nd,Dy)-containing SiAlON powders prepared by combustion synthesis

Preparation of (ca+m) (m=mg, Yb, Sr) Co-Doped Α-Sialon Powders by Combustion Synthesis

Fabrication of yttrium-stabilized α -SiAlON powders with rod-like crystals by combustion synthesis

Effect of Diluents and NH4F Additive on the Combustion Synthesis of Yb Α-Sialon

Effects of starting compositions on the phase composition and microstructure of Yb α-SiAlON prepared by combustion synthesis

Phase transformation and growth of rod-like α-SiAlON particles during combustion synthesis

Fabrication of one-dimensional rod-like α-SiAlON powders in large scales by combustion synthesis

Combustion synthesis of rod-like Yb alpha-sialon powders

Carbothermal Reduction Nitridation of Fly Ash, Diatomite and Raw Illite: Formation of Nitride Powders with Different Morphology and Photoluminescence Properties

Fabrication of (ca + Yb)- and (ca + Sr)-stabilized Α-Sialon by Combustion Synthesis

Solid-state NMR and XRD study of α-SiAlON powders prepared by combustion synthesis

Effect of seed addition with combustion synthesized powder on pressureless sintering of Y alpha-SiAlON

Improving Multifunctional Performance of Dy-doped (ba0.85ca0.15)(zr0.1ti0.9)o< Sub>3 Ceramics Via Tailoring Dy-doping Amount and Ceramic Processing

Effects Of Technical Parameters On The Phase Composition And Microstructure Of Yb Alpha-Sialon Prepared By Combustion Synthesis

Preparation of Y-SiAlON rod-like crystals and whiskers by combustion synthesis

Microstructure and Thermo‐Kinetics Analysis in Combustion Synthesis of Si3N4 with High α‐Phase Content

Effect of Fe‐Contained Species on the Preparation of Α‐si3n4 Fibers in Combustion Synthesis

Composition controlled microstructure and mechanical properties of Yb/Lu co-doped SiAlON

Effect of Nitrogen Pressure and Additives on Combustion Synthesis of Rod-Like Yttrium α-SiAlON Crystals

Combustion Synthesis of β-Si<sub>3</sub>N<sub>4</sub> and β-SiAlON with Elongated Prismatic Micro-Crystals by Adding SrCO<sub>3</sub> and NH<sub>4</sub>F

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f