Deformation Behavior of Mg–Zn–Gd-based Alloys Reinforced with Quasicrystal and Laves Phases at Elevated Temperatures

Yong Liu,Guangyin Yuan,Wenjiang Ding,Cheng Lu

DOI: https://doi.org/10.1016/j.jallcom.2006.03.027

IF: 6.2

2006-01-01

Journal of Alloys and Compounds

Abstract:Mg–Zn–Gd and Mg–Zn–Gd–Cu alloys, reinforced with quasicrystal (I-phase) and Laves phases, have been produced by extrusion process. The deformation behavior of these two alloys at room temperature and at elevated temperatures was investigated, respectively. The Mg–Zn–Gd alloy has high UTS of 305MPa and elongation of 14.6% due to the strengthening effect of I-phase, while Mg–Zn–Gd–Cu alloy with Laves phases has higher yield stress of 217MPa due to more strengthening particles and lower elongation of 11.9% resulting from the low content of I-phase and low symmetry of Laves phase due to which it cleaves easily (while the I-phase has a very high symmetry and therefore isotropic in nature). At high temperatures, Mg–Zn–Gd alloy shows large strain due to the excellent plastic compatibility coming from low interfacial energy of I-phase/matrix; Mg–Zn–Gd–Cu alloy has higher level of flow stress, strain exponent and more stable microstructure than Mg–Zn–Gd alloy due to better heat-resistance supplied by collaboration of Laves phases and quasicrystal phase, which can provide more effective pinning effect and suppress grain growth during deformation.