Influence of Low Frequency Electromagnetic Field on Microstructures of Semi-Continuously Cast High-Strength Al Alloy
YAN Ying,ZHANG Cai-bei,CUI Jing-lei,CUI Jian-zhong
DOI: https://doi.org/10.3321/j.issn:1004-0609.2005.03.016
2005-01-01
The Chinese Journal of Nonferrous Metals
Abstract:Microstructures of semi-continuously cast d100mm Al alloy ingot at different current intensities and frequencies were studied in details by optical microscope, X-ray diffraction and TEM to investigate the effect of electromagnetic field on microstructures of ingot. When current increases from 60 to 100A at 25Hz, the grains are gradually refined; When current is 100A, the optimum frequency of grain refinement is 25Hz. In contrast to the as-cast ingot, with the increase of current, texture produced along [311] direction gradually eliminates, and lattice constants at the center and edge of the ingot are more and more close, which shows that the distribution of solute atoms is more uniform. At current of 100A and frequency of 25Hz, width of precipitate-free zones on both sides of grain boundary becomes narrower and is about 100nm, the size of precipitates deposited both inside grains and along grain boundaries becomes smaller, and there exists metastable phase, with basically granular shapes.