Effect of Low Frequency Electromagnetic Casting on Microstructure and Properties of 4045 Alloy

QIN Ke,Jianzhong Cui

DOI: https://doi.org/10.3321/j.issn:1001-4977.2006.12.007

2006-01-01

Abstract:Under low frequency electromagnetic field,4045 alloys were semi-continuously cast into ingots with 100 mm in diameter.Microstructures of samples taken from different part of the cast with different cooling conditions were characterized by optical microscopy and scanning electron microscopy(SEM).Unlike casting without electromagnetic field,the α-Al dendrites were found to be thin and homogeneous under low frequency electromagnetic field.The eutectic Si grains are homogeneous with fine dimensions.Also,the Si-rich region formed at the edge of the ingot was found to be significantly decreased under low frequency electromagnetic field.The content of silicon in the primary aluminum reached to 2.59 %(wt).The mechanical properties of the electromagnetic modifying casting 4045 aluminum alloy improved with σb(ultimate tensile strength)of 225 MPa,ψ(elongation percentage)of 11.36% and HV(Vickers diamond hardness) of 69.5 MPa.