Abstract:Aluminum alloys, characterized by their low density and high mechanical strength, are widely applied in the manufacturing sector. However, the application of aluminum alloys in extreme environments presents severe corrosion challenges. Sol–gel organic coating techniques have garnered significant attention due to their excellent stability, barrier properties, and cost-effectiveness, as well as their simpler processing. Nevertheless, conventional sol–gel coatings are unable to withstand the corrosive effects of high-chloride and high-halide ion environments such as marine conditions, owing to their inherent structural defects. Therefore, this study proposes the utilization of a simple method to synthesize catechol (CA) and meta-phenylenediamine (MPD)-derived catecholamine compounds to modify sol–gel coatings. Surface characteristics of the modified coatings were analyzed using Fourier-transform infrared spectroscopy (FT-IR), ultraviolet-visible (UV-Vis) spectroscopy, scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). The thickness of the modified coating was approximately 6.8 μm. The CA/MPD-modified substance effectively densifies the sol–gel coating, enhancing its corrosion protection performance. A 3.5 wt% NaCl solution was used to simulate a marine environment, and electrochemical impedance spectroscopy (EIS) was conducted using an electrochemical workstation to evaluate the coating's protective properties over a long-term period. The results indicate that the modified coating provides protection for 3003 aluminum alloy for a minimum of 30 days under corrosive conditions, outperforming unmodified sol–gel coatings in terms of corrosion resistance.

Effect of Nano-SiO2 Hybrid Coatings on Corrosion Resistance of Aluminum Alloys

Preparation and Protective Effects of Nano-Tio2 Composite Coatings on LY12 Aluminum Alloys

A Sol–bath–gel Approach to Prepare Hybrid Coating for Corrosion Protection of Aluminum Alloy

Effect of Mixture Ratio on Water Uptake and Corrosion Performance of Silicone-Epoxy Hybrid Coatings Coated 2024 Al-alloy

Hybrid sol–gel coatings based on GPTMS/TEOS containing colloidal SiO2 and cerium nitrate for increasing corrosion protection of aluminium alloy 7075-T6

Effect of a Silane Coupling Agent on Corrosion Performance of Tetraethoxysilane Hybrid Coating

Cobaltous Acetate Doped Sol-gel Coatings for Corrosion Protection on Aluminium Alloy LY12

Corrosion resistance properties of organic–inorganic hybrid coatings on 2024 aluminum alloy

Optimization of Sol–gel Coatings on the Surface of Aluminum Pigments for Corrosion Protection

Characterization and corrosion protection of nano-titanium dioxide doped BTSE-GPTMS sol–gel coating on cast Al–Si alloy

Catechol/m-Phenylenediamine Modified Sol–Gel Coating with Enhanced Long-Lasting Anticorrosion Performance on 3003 Al Alloy

Hybrid Organosilicon-Metal oxide Composites and their Corrosion Protection Performance for Mild Steel in 3.5% NaCl Solution

Corrosion inhibition of flaky aluminium by sol-gel coatings of MTES and TEOS

Preparation and characterization of anticorrosion Ormosil sol–gel coatings for aluminum alloy

Study on Corrosion Resistance Properties of Organic-inorganic Hybrid Coatings on LY12 Aluminum Alloy

Corrosion Performance of Nano-Alumina Coatings over Anodized Aluminum Alloy by Dip Coating Method

Corrosion Resistance of Lamellar Aluminium Pigments Coated by SiO2 by Sol–gel Method

Effect of Silica Nanoparticles on Performance of Sol-Gel Coatings

Effect of Cerium Acetate Doping on Corrosion Behavior of Sol-Gel Coatings on 2a12 Aluminum Alloy

Effect of Silica Sol on Corrosion Resistance of Aluminum Phosphate Composite Coatings

Investigation on a Sol-gel Coating Containing Inhibitors on 2024-T3 Aluminum Alloy