Improvement of the Performances of Tubular Solid Oxide Fuel Cells by Optimizing Co-Sintering Temperature of the NiO/YSZ Anode-Ysz Electrolyte Double Layers

Dehua Dong,Mingfei Liu,Yingchao Dong,Bin Lin,Jiakui Yang,Guangyao Meng

DOI: https://doi.org/10.1016/j.jpowsour.2007.06.054

IF: 9.2

2007-01-01

Journal of Power Sources

Abstract:The effects of co-sintering temperature on anode microstructure, electrolyte film microstructure, and final cell performance of tubular solid oxide fuel cells (SOFCs) were fully studied. The co-sintering of the NiO/YSZ anode-YSZ electrolyte double layers at temperature ranging from 1350 to 1400°C for 5h was carried out. Porosity and electrical conductivity were measured to examine the anodes microstructure, and the electrolyte films microstructure were characterized by scanning electronic microscope (SEM). A higher open current voltage (OCV) value of 0.99V was achieved by co-sintering the cell at 1400°C indicating denser electrolyte film, while the maximum power density of the cell co-sintered at 1380°C was achieved with 322mWcm−2 at 800°C, which was higher than that (241.3mWcm−2) of the cell co-sintered at 1400°C because of better anode microstructure.