Abstract:CeO2 film plays an essential role in nucleation and growth of YBa2Cu3O7−x (YBCO) films. In this work, the dependence of superconducting properties of YBCO on CeO2 films with different thicknesses was investigated, in order to achieve fabrication of high-performance YBCO coated conductors in industrial scale. The crystalline structure and morphology of CeO2 films with thickness ranging from 21 to 563 nm were systematically characterized by means of X-ray diffraction (XRD), atomic force microscope (AFM) and reflection high-energy electron diffraction (RHEED). Additional focus was addressed on evolution of the surface quality of CeO2 films with thickness increasing. The results show that at the optimal thickness of 221 nm, CeO2 film exhibits sharp in-plane and out-of-plane texture with full width of half maximum (FWHM) values of 5.9° and 1.8°, respectively, and smooth surface with a mean root-mean-square (RMS) roughness value as low as 0.6 nm. Combing RHEED and transmission electron microscope (TEM) cross-sectional analysis, it is found that nucleation and growth of CeO2 films at early stage remain in island growth mode with rougher surface, while further increasing the thickness beyond the optimal thickness leads to weak surface quality, consequently resulting in degradation of superconductor layers deposited subsequently. Eventually, a critical current density (J c) as high as 4.6 × 106 A·cm−2 (77 K, self-field) is achieved on a YBCO film on a thickness-modulated CeO2/MgO/Y2O3/Al2O3/C276 architecture, demonstrating the advantages of CeO2 films as buffer layer in high-throughput manufacture of coated conductors.

Preparation of YBCO Film for Microwave Filter Using a Hybrid Route

Fabrication of YBCO Coated Conductors on Biaxial Textured Metal Substrate by All-Sputtering

Development of High Critical Current YBCO Coated Conductors by Photo-Assisted MOCVD

MOCVD Preparation of YBCO Coated Conductors on CeO2/YSZ/Y2O3 Buffered RABiTS Substrate

Simultaneous double-sided deposition of long-length epitaxial CeO 2 buffer layers for YBCO coated conductors

Preparation and Characterization of Ceo2/Ysz/Ceo2 Buffer Layers for Ybco Coated Conductors

Epitaxial growth of YBCO thin films on LaAlO3 substrate with CeO2 buffer layer

Progress towards a low-cost commercial coated conductor

Single Cerium Zirconate Buffer Layer on Biaxially Textured Metal Substrates for High Performance Coated Conductors

In-situ Preparation of YBCO Thin Films on Single Crystal LaAlO<Subscript>3</Subscript>

Preparation of φ3-inch large-area double-sided YBCO thin film on CeO2 buffered r-plane sapphire

Dependence of Microstructure and J C of YBCO Films on CeO 2 Cap Layers Deposited by Multi-plume PLD

In-situ Preparation of YBCO Thin Films on Single Crystal LaAlO3

Reel-To-Reel Continuous Deposition Of Ce(X)Zr(1-X)O(2) Single Buffer Layer For Ybco Coated Conductors

Thickness Modulation Effect of CeO2 Layer for YBCO Films Grown by Pulsed Laser Deposition

A Novel Process for Ceo2 Single Buffer Layer on Biaxially Textured Metal Substrates in Ybco Coated Conductors

MOCVD Derived Double-Sided YBa2Cu3O7−δ Films on Y2O3/YSZ/CeO2 Buffered Textured Metal Substrates

Fabrication and Characterization of La2Zr2O7 Films on Different Buffer Architectures for YBa2Cu3O7−δ Coated Conductors by RF Magnetron Sputtering

Microstructure Analysis of High-Quality Buffer Layers on Textured Niw Tapes for Ybco Coated Conductors

Ethanol-based TFA–MOD Method for Preparation of YBCO Films

A New Direct Process to Prepare YBa2Cu3O7- films on Biaxially Textured Ag{110}<211>