Abstract:ZnO nanorods were grown on ITO substrates with different concentration of electrolyte by electrodeposition method. Microstructure, surface topography, photoluminescence Spectra, Raman spectra and water contact angle of the thin films were measured. The XRD results show all samples are hexagonal wurtzite and the intensity of diffraction peaks at (002) preferred orientation are strengthen as electrolyte concentration increase from 0.005 to 0.03 M. As the concentration increases, the average diameter, density and inclination of the ZnO nanorods increased. Room temperature photoluminescence spectras of the ZnO nanorods show a narrow UV band centering at about 377 nm and broad visible emissions around 600 nm and the UV peak intensity revealed a remarkable decreased. Raman spectras exhibit three peaks which are located at 439 cm(-1), 562 cm(-1) and 1095 cm(-1). All samples change from hydrophobicity to hydrophilic after one hour ultraviolet (UV) irradiation. (C) The Author(s) 2015. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution Non-Commercial No Derivatives 4.0 License (CC BY-NC-ND, http://creativecommons.org/licenses/by-nc-nd/4.0/), which permits non-commercial reuse, distribution, and reproduction in any medium, provided the original work is not changed in any way and is properly cited. For permission for commercial reuse, please email: oa@electrochem.org. All rights reserved.

Preparation and Characterization of Magnesium Oxide Nanorods

Synthesis of Magnesium Borate Nanorods by Sol-Gel Process

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Preparation and Characterization of Mg(OH) 2 Nanorods by Liquid–solid Arc Discharge Technique

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Preparation of Mg(Oh)(2) Nanorods

Preparation And Characterization Of Bismuth Sulfide Single Crystal Nanorods In Ionic Liquids

Preparation and characterization of ZnO nanorods

Synthesis and Characterization of MgO Single-Crystalline One-Dimensional Nanostructures

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Preparation and characterization of bat-like ZnO micro- and nanorods by adjusting oxygen flux

Fabrication and Characterization of One Dimention Magnesium Hydroxide Nanomaterials

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Nanosized MgO Powder Preparation by Homogeneous Precipitation-Post Annealing Method Using Mg(NO3)2·6H2O as Raw Material

Bulk Mg-doped Spherical Lithium Cobalt Oxide Preparation and Characterization of Precursor

Preparation and Characterization of Porous Mgo and Nio/Mgo Nanocomposites

[The Study on the Growth Process of ZnO Nanorods].

Preparation and characterization of lamellar-like Mg(OH)2 nanostructures via natural oxidation of Mg metal in formamide/water mixture

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Preparation and characterization of NiO nanorods by thermal decomposition of NiC2O4 precursor

Hydrothermal Preparation of ZnO Nanorods Using Zinc Powder As Precursor and Their Characterization