Fabrication of Silver-Coated Hollow Fiber with an Inner Diameter of 100 µm or Less
Katsumasa Iwai,Mitsunobu Miyagi,Yi-Wei Shi,Yuji Matsuura
DOI: https://doi.org/10.1117/12.874087
2011-01-01
Abstract:Extremely flexible hollow fibers with 100-mu m-bore size or less were developed for infrared laser delivery. Fabrication process and transmission properties of the ultra-thin hollow fiber were discussed. The silver layer was inner-plated by using the conventional silver mirror-plating technique. Concerning the fabrication parameters used up to now for 320-mu m bore-sized fibers, the target flowing rate for plating solutions was 10 ml/min. Parallel bundles of silica capillary were used to increase the cross-sectional area. To achieve the target, bundles with 560 pieces, 1200 pieces, and 9600 pieces were used for the capillary with inner diameters of 100-mu m, 75-mu m, and 50-mu m, respectively. The loss for the 50-mu m bore size, 10-cm length silver hollow fiber was 10 dB at the wavelength of 1 mu m.